Mesoporous silica particles of MCM-41 type were synthesized by sol-gel method from tetraethyl orthosilicate (TEOS) in 2-methoxyethanol and deionized water mixture in base conditions at room temperature. Ammonia or sodium hydroxides were used as catalysts and cetyl-trimethylammonium bromide (CTAB) and n-dodecyl-trimethylammonium bromide (DTAB) as structure directing agents. The porosities and the ordered structure have been analyzed using transmission and scanning electron microscopy, small angle neutron and X-ray diffraction, nitrogen adsorption, thermal analysis and FTIR spectroscopy. The samples consist of spherical particles of sub-micrometer size, with radially arranged pores. The comparison of the effect of the different surfactants and catalysts shows that by varying the surfactant type and their proportion, the pore sizes can be controlled. As compared to the commonly used ammonia catalyst, the use of NaOH as catalyst results in a much smaller porosity of the as-prepared materials. These materials are not resisting to the heat treatment at 700 C used for the template removal, and the ordered porous structure is completely lost.
Atomic layer deposition (ALD) enables the conformal coating of porous materials, making the technique suitable for pore size tuning at the atomic level, e.g., for applications in catalysis, gas separation and sensing. It is, however, not straightforward to obtain information about the conformality of ALD coatings deposited in pores with diameters in the low mesoporous regime (< 10 nm). In this work, it is demonstrated that in situ synchrotron based grazing incidence small angle x-ray scattering (GISAXS) can provide valuable information on the change in density and internal surface area during …
Mesoporous silica matrices have been prepared via classic acid catalyzed and sono-catalyzed sol-gel routes. Tetramethoxysilan (TMOS) and methyl-trimethoxysilane (MTMS) were used as silica precursors, and N-butyl-3-methylpyridinium tetrafluoroborate ([bmPy][BF4]) was employed as co-solvent and pore template. The ionic liquid (IL) to silica mole ratio was varied between 0.007 and 0.07. Nitrogen adsorption-desorption and small-angle neutron scattering measurements were used to characterize the obtained materials. The ionic liquid played the role of catalyst that affected the formation of the prim…
We study water adsorption-induced deformation of a monolithic, mesoporous silicon membrane traversed by independent channels of $\sim$8 nm diameter. We focus on the elastic constant associated with the Laplace pressure-induced deformation of the membrane upon capillary condensation, i.e. the pore-load modulus. We perform finite-element method (FEM) simulations of the adsorption-induced deformation of hexagonal and square lattices of cylindrical pores representing the membrane. We find that the pore-load modulus weakly depends on the geometrical arrangement of pores, and can be expressed as a f…
Understanding mechanisms in DSSCs is fundamental for their improvement; this includes the nanocrystalline semiconducting layer behaviour. Different mesoporous TiO2 layers are fabricated and analyzed for possible use in DSSC solar cells. The preparations included the addition of P123 triblock copolymer as structuring agent to the synthesized anatase sol. This preparation was also mixed with Degussa P25 nanoparticles in one case and polystyrene latex in another. Mesoporous mixed TiO2-SiO2 thin layers were also analyzed. The diverse morphology and features are studied by microscopic techniques an…
Silicon nanowires are prepared by the method of the two-step metal-assisted wet chemical etching. We have analyzed the structure of solid, rough and porous nanowire surfaces of boron-doped silicon substrates with resistivities of ρ> 1000 Ωcm, ρ= 14-23 Ωcm, ρ< 0.01 Ωcm by scanning electron microscopy and nitrogen gas adsorption. Silicon nanowires prepared from highly-doped silicon reveal mesopores on their surface. However, we found a limit for pore formation. Pores were only formed by etching below a critical H$_2$O$_2$ concentration (c$_{\mbox{H}_2\mbox{O}_2}$ < 0.3 M). Furthermore, we have d…
The structural and dynamical properties of water confined in nanoporous silica with a pore diameter of 2.7 nm were investigated by performing large-scale molecular dynamics simulations using the reactive force field. The radial distribution function and diffusion coefficient of water were calculated, and the values at the center of the pore agreed well with experimental values for real water. In addition, the pore was divided into thin coaxial layers, and the average number of hydrogen bonds, hydrogen bond lifetime, and hydrogen bond strength were calculated as a function of the radial distanc…
Mesoporous silica particles have been synthesized by sol-gel method from tetraethoxysilane (tetraethylorthosilicate, TEOS) and methyltriethoxysilane (MTES), in ethanol and water mixture, at different ratios of the of the silica precursors. Ammonia was used as catalyst at room temperature and hexadecyltrimethylammonium bromide (cetyltrimethylammonium bromide, CTAB) as the structure directing agent. Nitrogen sorption, X-ray diffraction and small-angle neutron scattering gave information on the evolution of the gel structure and pore morphologies in the function of MTES/TEOS molar ratio. Thermogr…
We present a capacitance method to measure the adsorption of rod-like nematogens (4-cyano-4'-pentylbiphenyl, 5CB) from a binary liquid 5CB/methanol solution into a monolithic mesoporous silica membrane traversed by tubular pores with radii of 5.4 nm at room temperature. The resulting adsorption isotherm is reminiscent of classical type II isotherms of gas adsorption in mesoporous media. Its analysis by a model for adsorption from binary solutions, as inspired by the Brunauer-Emmett-Teller (BET) approach for gas adsorption on solid surfaces, indicates that the first adsorbed monolayer consists …
Formation and Thermodynamic Behavior of THF-Water Hydrates in Confined Mesoporous Media
Institute of Physics of Rennes, CNRS-University of Rennes 1（雷恩物理研究所，法国国家科学研究中心-雷恩第一大学）；Laboratoire Léon Brillouin（莱昂·布里渊实验室）；Institut des Sciences moléculaires, UMR5255 CNRS – Université de Bordeaux（分子科学研究所，法国国家科学研究中心-波尔多大学）
Condensation, melting and freezing of nitrogen in a powder of mesoporous silica grains (SBA-15) has been studied by combined volumetric sorption isotherm and scanning calorimetry measurements. Within the mean field model of Saam and Cole for vapor condensation in cylindrical pores a liquid nitrogen sorption isotherm is well described by a bimodal pore radius distribution. It encompasses a narrow peak centered at 3.3 nm, typical of tubular mesopores, and a significantly broader peak characteristic of micropores, located at 1 nm. The material condensed in the micropores as well as the first two …
In this paper, we present measurements of the ortho-positronium emission energy in vacuum from mesoporous films using the time of flight technique. We show evidence of quantum mechanical confinement in the mesopores that defines the minimal energy of the emitted Ps. Two samples with different effective pore sizes, measured with positron annihilation lifetime spectroscopy, are compared for the data collected in the temperature range 50-400 K. The sample with smaller pore size exhibits a higher minimal energy ($73\pm$5 meV), compared to the sample with bigger pores ($48\pm$5 meV), due to the str…
We present gravimetrical, optical, and neutron imaging measurements of the capillarity-driven infiltration of mesoporous silica glass by hydrocarbons. Square-root-of-time Lucas-Washburn invasion kinetics are found for linear alkanes from n-decane (C10) to n-hexacontane (C60) and for squalane, a branched alkane, in porous Vycor with 6.5 nm or 10 nm pore diameter, respectively. Humidity-dependent experiments allow us to study the influence on the imbibition kinetics of water layers adsorbed on the pore walls. Except for the longest molecule studied, C60, the invasion kinetics can be described by…
The adsorption of lysozyme, cytochrome c and myoglobin, similar-sized globular proteins of approximately 1.5 nm radius, into the mesoporous silica material Santa Barbara Amorphous-15 (SBA-15) with 3.3 nm mean pore radius has been studied photometrically for aqueous solutions containing a single protein type and for binary protein mixtures. Distinct variations in the absolute and relative adsorption behavior are observed as a function of the solution's pH-value, and thus pore wall and protein charge. The proteins exhibit the strongest binding below their isoelectric points pI, which indicates t…
The linear 1-alcohols n-C16H33OH, n-C17H35OH, n-C19H37OH have been imbibed and solidified in lined up, tubular mesopores of silicon with 10 nm and 15 nm mean diameters, respectively. X-ray diffraction measurements reveal a set of six discrete orientation states (''domains'') characterized by a perpendicular alignment of the molecules with respect to the long axis of the pores and by a four-fold symmetry about this direction, which coincides with the crystalline symmetry of the Si host. A Bragg peak series characteristic of the formation of bilayers indicates a lamellar structure of the spatial…
We present, along with some fundamental concepts regarding imbibition of liquids in porous hosts, an experimental, gravimetric study on the capillarity-driven invasion dynamics of water and of the rod-like liquid crystal octyloxycyanobiphenyl (8OCB) in networks of pores a few nanometers across in monolithic silica glass (Vycor). We observe, in agreement with theoretical predictions, square root of time invasion dynamics and a sticky velocity boundary condition for both liquids investigated. Temperature-dependent spontaneous imbibition experiments on 8OCB reveal the existence of a paranematic p…
The lattice dynamics of preferentially aligned nanocrystals formed upon drying of aqueous Ba(NO$_3$)$_2$ solutions in a mesoporous silica glass traversed by tubular pores of approximately 12 nm are explored by Raman scattering. To interpret the experiments on the confined nanocrystals polarized Raman spectra of bulk single crystals and X-ray diffraction experiments are also performed. Since a cubic symmetry is inherent to Ba(NO$_3$)$_2$, a special Raman scattering geometry was utilized to separate the phonon modes of A$_g$ and E$_g$ species. Combining group-theory analysis and \textit{ab initi…
In this work the synthesis of ZrO$_{2}$-CeO$_{2}$ and ZrO$_{2}$-CeO$_{2}$/SiO$_{2}$ were developed, based on the process to form ordered mesoporous materials such as SBA-15 silica. The triblock copolymer Pluronic P-123 was used as template, aiming to obtain crystalline single phase walls and larger specific surface area, for future applications in catalysis. SAXS and XRD results showed a relationship between ordered pores and the material crystallization. 90% of CeO$_{2}$ leaded to single phase homogeneous ceria-zirconia solid solution of cubic fluorite structure (Fm$\bar{3}$m). The SiO$_{2}$ …
Achieving high power performance and durability with low Pt loadings are critical challenges for proton exchange membrane fuel cells. PtCo catalysts developed on new carbon black supports show promise by simultaneously providing good oxygen reduction kinetics and local oxygen transport. We investigate the role of nanoscale morphology in the performance of these catalysts supported on accessible (HSC-e and HSC-f) and conventional (Ketjen Black) porous carbons using 3D electron tomography, nitrogen sorption, and electrochemical performance measurements. We find that the accessible porous carbons…
We present gravimetrical and optical imaging experiments on the capillarity-driven imbibition of silicone oils in monolithic silica glasses traversed by 3D networks of pores (mesoporous Vycor glass with 6.5 nm or 10 nm pore diameters). As evidenced by a robust square-root-of-time Lucas-Washburn (L-W) filling kinetics, the capillary rise is governed by a balance of capillarity and viscous drag forces in the absence of inertia and gravitational effects over the entire experimental times studied, ranging from a few seconds up to 10 days. A video on the infiltration process corroborates a collecti…
Combining dielectric crystals with mesoporous solids allows a versatile design of functional nanomaterials, where the porous host provides a mechanical rigid scaffold structure and the molecular filling adds the functionalization. Here, we report a study of the complex lattice dynamics of a SiO$_2$:KH$_2$PO$_4$ nanocomposite consisting of a monolithic, mesoporous silica glass host with KH$_2$PO$_4$ nanocrystals embedded in its tubular channels $\sim$12 nm across. A micro-Raman investigation performed in the spectral range of 70-1600 cm$^{-1}$ reveals the complex lattice dynamics of the confine…
We report dielectric relaxation spectroscopy experiments on two rod-like liquid crystals of the cyanobiphenyl family (5CB and 6CB) confined in tubular nanochannels with 7 nm radius and 340 micrometer length in a monolithic, mesoporous silica membrane. The measurements were performed on composites for two distinct regimes of fractional filling: monolayer coverage at the pore walls and complete filling of the pores. For the layer coverage a slow surface relaxation dominates the dielectric properties. For the entirely filled channels the dielectric spectra are governed by two thermally-activated …