Single atom metallic wires of arbitrary length are of immense technological and scientific interest. We describe a novel silicon-only template enabling the self-organised growth of isolated micrometer long surface and subsurface single-atom chains. It consists of a one dimensional, defect-free reconstruction - the Haiku core, here revealed for the first time in details - self-assembled on hydrogenated Si(001) terraces, independent of any step edges. We discuss the potential of this Si-in-Si template as an appealing alternative to vicinal surfaces for nanoscale patterning.
Template-assisted synthesis is a facile way of growing various one-dimensional nanostructures. Among various nanoporous templates, anodic aluminium oxide (AAO) is most commonly used. In this work, the kinetics of silver nanowire growth by electrodeposition in AAO templates was investigated. The AAO templates were fabricated using the standard two-step anodisation process. The geometrical features of the fabricated templates, such as pore diameter (55 nm), interpore distance (115 nm), wall thickness (27 nm), porosity (19.87 %), and pore density were obtained using scanning electron microscopy. …
Strained trigonal Te has been predicted to host Weyl nodes supported by a non-symmorphic chiral symmetry. Using low-pressure physical vapor deposition, we systematically explored the growth of trigonal Te nanowires with naturally occurring strain caused by curvature of the wires. Raman spectra and high mobility electronic transport attest to the highly crystalline nature of the wires. Comparison of Raman spectra for both straight and curved nanowires indicates a breathing mode that is significantly broader and shifted in frequency for the curved wires. Strain induced by curvature during growth…
Integration of high quality semiconductor-superconductor devices into scalable and CMOS compatible architectures remains an outstanding challenge, currently hindering their practical implementation. Here, we demonstrate growth of InAs nanowires monolithically integrated on Si inside lateral cavities containing superconducting TiN elements. This technique allows growth of hybrid devices characterized by sharp semiconductor-superconductor interfaces and with alignment along arbitrary crystallographic directions. Electrical characterization at low temperature reveals proximity induced superconduc…
Self-assembled Ge wires with a height of only 3 unit cells and a length of up to 2 micrometers were grown on Si(001) by means of a catalyst-free method based on molecular beam epitaxy. The wires grow horizontally along either the [100] or the [010] direction. On atomically flat surfaces, they exhibit a highly uniform, triangular cross section. A simple thermodynamic model accounts for the existence of a preferential base width for longitudinal expansion, in quantitative agreement with the experimental findings. Despite the absence of intentional doping, first transistor-type devices made from …
Semiconductor nanowires have been playing a crucial role in the development of nanoscale devices for the realization of spin qubits, Majorana fermions, single photon emitters, nanoprocessors, etc. The monolithic growth of site-controlled nanowires is a prerequisite towards the next generation of devices that will require addressability and scalability. Here, combining top-down nanofabrication and bottom-up self-assembly, we report on the growth of Ge wires on pre-patterned Si (001) substrates with controllable position, distance, length and structure. This is achieved by a novel growth process…
We report growth and characterization of a coupled quantum dot structure that utilizes nanowire templates for selective epitaxy of radial heterostructures. The starting point is a zinc blende InAs nanowire with thin segments of wurtzite structure. These segments have dual roles: they act as tunnel barriers for electron transport in the InAs core, and they also locally suppress growth of a GaSb shell, resulting in coaxial InAs-GaSb quantum dots with integrated electrical probes. The parallel quantum dot structure hosts spatially separated electrons and holes that interact due to the type-II bro…
Topological qubits based on Majorana fermions have the potential to revolutionize the emerging field of quantum computing by making information processing significantly more robust to decoherence. Nanowires (NWs) are a promising medium for hosting these kinds of qubits, though branched NWs are needed to perform qubit manipulations. Here we report gold-free templated growth of III-V NWs by molecular beam epitaxy using an approach that enables patternable and highly regular branched NW arrays on a far greater scale than what has been reported thus far. Our approach relies on the lattice-mismatch…
Sub-wavelength laser induced periodic surface structures (LIPSS-Sticks) created by ultrashort pulsed laser irradiation on the surface of titanium are used for the first time to template the electrochemical growth of titanium dioxide nanotube arrays. This is an example of a double self-organized process, as both LIPSS formation and electrochemical anodization involve spontaneous generation of order from initially non-ordered precursors. LIPSS-Sticks have a 2x greater visible to near infrared light (400 - 1400 nm) collection efficiency compared to flat titanium dioxide due to the enhanced light …
We have measured the resistances (and resistivities) of Ag and Cu nanowires of diameters ranging from 15nm to 200nm in the temperature range 4.2K-300K with the specific aim to assess the applicability of the Bloch-Grüneisen formula for electron phonon resistivity in these nanowires. The wires were grown within polymeric templates by electrodeposition. We find that in all the samples the resistance reaches a residual value at T=4.2K and the temperature dependence of resistance can be fitted to the Bloch-Grüneisen formula in the entire temperature range with a well defined transport Debye temper…
Self-selective growth of GaAs1-xBix on GaAs zinc blende/wurtzite nanowire heterostructures
Lund University（隆德大学）；NanoLund, Lund University（隆德大学纳米隆德）；Centre for Analysis and Synthesis, Lund University（隆德大学分析与合成中心）；MAX IV Laboratory, Lund University（隆德大学MAX IV实验室）；Niels Bohr Institute, University of Copenhagen（哥本哈根大学尼尔斯玻尔研究所）
A density functional theory study of the structural and electronic properties and relative stability of narrow SP3 silicon nanotubes of different growth orientations is presented. All nanotubes studied and their corresponding wire structures are found to be meta-stable with the wires being more energetically stable. Silicon nanotubes show a dramatic bandgap increase of up to 68% with respect to the corresponding wires. Furthermore, a direct relation between the bandgap of the system and the molar fraction of the passivating hydrogen contents is found. These results suggest that by careful cont…
We present controlled growth of c(2$\times$2)N islands on the (100) surface of Cu$_3$Au, which can be used as an insulating surface template for manipulation of magnetic adatoms. Compared to the commonly used Cu(100)/c(2$\times$2)N surface, where island sizes do not exceed several nanometers due to strain limitation, the current system provides better lattice matching between metal and adsorption layer, allowing larger unstrained islands to be formed. We show that we can achieve island sizes ranging from tens to hundreds of nanometers, increasing the potential building area by a factor 10$^3$.…
High-quality T-shaped quantum wires are fabricated by cleaved-edge overgrowth with the molecular beam epitaxy on the interface improved by a growth-interrupt high-temperature anneal. Characterization by micro-photoluminescence (PL) and PL excitation (PLE) spectroscopy at 5 K reveals high uniformity, a sharp spectral width, and a small Stokes shift of one-dimensional (1-D) excitons. The PLE spectrum for 1-D states shows a large peak of ground-state excitons and a small absorption band ascribed to 1-D continuum states with an onset at 11 meV above the exciton peak.
Cutting-edge research in the band engineering of nanowires at the ultimate fine scale is related to the minimum scale of a nanowire-based device. The fundamental issue at the subnanometre scale is whether angle-resolved photoemission spectroscopy (ARPES) can be used to directly measure the momentum-resolved electronic structure of a single wire because of the difficulty associated with assembling single wire into an ordered array for such measurements. Here, we demonstrated that the one-dimensional (1D) confinement of electrons, which are transferred from external dopants, within a single subn…
The observation of intense visible fluorescence from silver and iron nanoparticles in different solution phases and surface capping is reported here. Metallic silver and iron nanoparticles were obtained by exploding pure silver and iron wires in pure water. Bovine serum albumin protein adsorption on the silver nanoparticles showed an enhanced fluorescence. The presence of poly-vinyl pyrrolidone polymer in the exploding medium resulted in a stabilized growth of iron nanoparticles with enhanced fluorescence intensity. The fluorescence was found to be surface /interface dependant. The fluorescenc…
The formation of nanostructures during metalorganic vapor-phase epitaxy on patterned (001)/(111)B GaAs substrates is reviewed. The focus of this review is on the seminal experiments that revealed the key kinetic processes during nanostructure formation and the theory and modelling that explained the phenomenology in successively greater detail. Experiments have demonstrated that V-groove quantum wires and pyramidal quantum dots result from self-limiting concentration profiles that develop at the bottom of V-grooves and inverted pyramids, respectively. In the 1950s, long before the practical im…
Heavy holes confined in quantum dots are predicted to be promising candidates for the realization of spin qubits with long coherence times. Here we focus on such heavy-hole states confined in Germanium hut wires. By tuning the growth density of the latter we can realize a T-like structure between two neighboring wires. Such a structure allows the realization of a charge sensor, which is electrostatically and tunnel coupled to a quantum dot, with charge-transfer signals as high as 0.3e. By integrating the T-like structure into a radio-frequency reflectometry setup, single-shot measurements allo…