We report the existence of a field-induced ferromagnetic transition in the magnetically ordered state (<69 K) of an intermetallic compound, Tb5Si3, and this transition is distinctly first-order at 1.8 K (near 60 kOe), whereas it appears to become second order near 20 K. The finding we stress is that the electrical resistivity becomes suddenly large in the high-field state after this transition and this is observed in the entire temperature range in the magnetically ordered state. Such an enhancement of 'positive' magnetoresistance (below 100 kOe) at the metamagnetic transition field is unexpected on the basis that the application of magnetic field should favor a low-resistive state due to alignment of spins.
We report the response of electrical resistivity $ρ$ to the application of magnetic fields (H) up to 140 kOe in the temperature interval 1.8-300 K for the compound, Gd7Rh3, ordering antiferromagnetically below 150 K. We find that there is an unusually large decrease of $ρ$ for moderate values of H in the close vicinity of room temperature uncharacteristic of paramagnets, with the magnitude of the magnetoresistance increasing with decreasing temperature as though the spin-order contribution to $ρ$ is temperature dependent. In addition, this compound exhibits giant magnetoresistance behaviour at…
Magnetization (M) and magnetoresistance (MR) measurements on polycrystalline R2Mn3Si5 (R = Tb, Dy and Ho) compounds (tetragonal, space group P4/mnc) have been carried out in the temperature range of 2 K-300 K, in various applied fields. Both, the rare earth and the Mn, are found to carry magnetic moments in these compounds. Mn has two sub-lattices (Mn1 and Mn2) that order magnetically at two different temperatures. Rare earth and Mn1 moments order ferromagnetically at TC1 whereas Mn2 is found to magnetically order at TC2 (TC1 = 89 K, 86 K, 78 K and TC2 = 18 K, 34 K, 16 K for R = Tb, Dy and Ho …
The results of dc magnetization, electrical and magnetoresistance and heat capacity measurements (2-300 K) on Tb7Rh3, crystallizing in Th7Fe3-type hexagonal structure, are reported. In this compound, magnetic ordering sets in around 90 K with additional transitions at low temperatures and the temperature coefficient of resistivity (R), dR/dT, is negative over a wide temperature range in the paramagnetic state. The present magnetization results reveal that this compound is apparently characterized by rich features in the magnetic-field-temperature phase diagram. A point of major emphasis is tha…
We report complex magnetic, magnetoresistance (MR) and magnetocaloric properties of Gd4RhAl and Tb4RhAl forming in the Gd4RhIn type cubic structure. Though the synthesis of the compounds was reported long ago, to our knowledge, no attempt was made to investigate the properties of these compounds. The present results of ac and dc magnetization, electrical resistivity and heat-capacity measurements down to 1.8 K establish that these compounds undergo antiferromagnetic order initially, followed by complex spin-glass features with decreasing temperature. These characteristic temperatures are: For …
The compound Dy7Rh3 ordering antiferromagnetically below (TN=) 59 K has been known to exhibit a temperature (T) dependent electrical resistivity (rho) behavior in the paramagnetic state unusual for intermetallic compounds in the sense that there is a broad peak in rho(T) in the paramagnetic state (around 130 K) as though there is a semi-conductor to metal transition. In addition, there is an upturn below T_N due to magnetic super-zone gap effects. Here we report the influence of external magnetic field (H) on the rho(T) behavior of this compound below 300 K. The rise of rho(T) found below TN c…
Tunneling surface current through a thin ferromagnetic barrier in a three-dimensional topological insulator is shown to possess an extraordinary response to the orientation of barrier magnetization. In contrast to conventional magnetoresistance devices that are sensitive to the relative alignment of two magnetic layers, a drastic change in the transmission current is achieved by a single layer when its magnetization rotates by 90 degrees. Numerical estimations predict a giant magnetoresistance as large as 800 % at room temperature and the proximate exchange interaction of 40 meV in the barrier…
Field-induced magnetization jumps with similar characteristics are observed at low temperature for the intermetallic germanide Gd5Ge4and the mixed-valent manganite Pr0.6Ca0.4Mn0.96Ga0.04O3. We report that the field location -and even the existence- of these jumps depends critically on the magnetic field sweep rate used to record the data. It is proposed that, for both compounds, the martensitic character of their antiferromagnetic-to-ferromagnetic transitions is at the origin of the magnetization steps.
Exchange bias effect is an important attribute in several device applications. Traditionally, it is discussed as a form of exchange anisotropy at the interface between the ferromagnetic/antiferromagnetic layers of two distinct systems. We report here on the magnetically ordered alloys possessing the feature of unidirectional anisotropy, which reverses its sign across a characteristic temperature. These are admixed rare earth intermetallics, comprising two dissimilar rare earth (RE) ions, belonging to the two different halves of the 4f-series and imbibing the notion of ferromagnetic coupling be…
Recent works aiming at understanding magnetotransport phenomena in ferromagnetic III-V and II-VI semiconductors are described. Theory of the anomalous Hall effect in p-type magnetic semiconductors is discussed, and the relative role of side-jump and skew-scattering mechanisms assessed for (Ga,Mn)As and (Zn,Mn)Te. It is emphasized that magnetotransport studies of ferromagnetic semiconductors in high magnetic fields make it possible to separate the contributions of the ordinary and anomalous Hall effects, to evaluate the role of the spins in carrier scattering and localization as well as to dete…
Novel thermal effects across the first order antiferromagnetic (AFM) - ferromagnetic (FM) transition in an intermetallic alloy are reported. They show instances of warming when heat is extracted from the sample, and cooling when heat is provided to the sample across AFM-FM transition in Ta doped $HfFe_2$, thus providing indisputable evidence of metastable supercooled AFM and superheated FM states, respectively. Such thermal effects in a magnetic solid prepared from commercially available materials has been reported for the first time. The transition proceeds in multiple steps which is interpre…
Based on magnetization, specific heat, magnetostriction, and neutron diffraction studies on single-crystal TbCo2B2C, it is found out that the paramagnetic properties, down to liquid nitrogen temperatures, are well described by a Curie-Weiss behavior of the Tb+3 moments. Furthermore, below Tc= 6.3 K, the Tb-sublattice undergoes a ferromagnetic (FM) phase transition with the easy axis being along the (100) direction and, concomitantly, the unit cell undergoes a tetragonal-to-orthorhhombic distortion. For fields up to 90 kOe, no field-induced splitting of the Co 3d orbitals was observed; as such …
In order to gain insights into the origin of colossal magneto-resistance (CMR) in manganese oxides, we performed a ^{139}La NMR study in the double-layered compound La_{1.2}Sr_{1.8}Mn_2O_7. We find that above the Curie temperature T_C=126 K, applying a magnetic field induces a long-range ferromagnetic order that persists up to T=330 K. The critical field at which the induced magnetic moment is saturated coincides with the field at which the CMR effect reaches to a maximum. Our results therefore indicate that the CMR observed above T_C in this compound is due to the field-induced ferromagnetism…
Low temperature scanning tunneling spectroscopy of HfNiSn shows a V^m(m < 1) zero bias anomaly around the Fermi level. This local density of states with a fractional power law shape is well known to be a consequence of electronic correlations. For comparison, we have also measured the tunneling conductances of other half-Heusler compounds with 18 valence electrons. ZrNiPb shows a metal-like local density of states, whereas ZrCoSb and NbFeSb show a linear and V^2 anomaly. One interpretation of these anomalies is that a correlation gap is opening in these compounds. By analyzing the magnetoresis…
We study the magnetic and transport properties of all-manganite heterostructures consisting of ferromagnetic metallic electrodes separated by an antiferromagnetic barrier. We find that the magnetic ordering in the barrier is influenced by the relative orientation of the electrodes magnetization producing a large difference in resistance between the parallel and antiparallel orientations of the ferromagnetic layers. The external application of a magnetic field in a parallel configuration also leads to large magnetoresistance.
C14 Nb(Fe89.4Al10.6)2 Laves phase intermetallic compound was investigated by DC magnetization (M) measurements performed in the temperature (T) interval of 20 to 175 K,under an applied magnetic field (H) ranging between 50 and 1250 Oe. Magnetization curves were recorded in the field-cooled (FC) and in the zero-field-cooled (ZFC) modes. They clearly showed an irreversible character that vanished at H=1250 Oe. Both magnetization curves exhibited well-defined peaks around T_N =72.3 K whose positions were H-independent, so they were identified as the compound's Néel temperature. The existence of i…
The compound, Nd7Rh3, crystallizing in Th7Fe3-type hexagonal structure, was previously known to exhibit two magnetic transitions, one at 32 K and the other at 10 K (in zero magnetic field). Here, we report the existence of a field-induced first-order antiferromagnetic to ferromagnetic transition at 1.8 K in this compound. On the basis of the measurements of isothermal magnetization and magnetoresistance, we provide evidence for the occurence of kinetic-hindrance, proposed in the literature, resulting in phase co-existence (super-cooled ferromagnetic + antifferomagnetic) and percolative electri…
In this paper, we have found a family of intermetallic compounds YMn12-xFex (x = 6.6-8.8) showing a bulk form of tunable giant exchange bias effect which arises from global interactions among ferromagnetic (FM) and antiferromagnetic (AFM) sublattices but not the interfacial exchange coupling or inhomogeneous magnetic clusters. A giant exchange bias with a loop shift up to 6.1 kOe has been observed in YMn4.4Fe7.6 compound with the strongest competing magnetic interactions. In a narrow temperature range, the exchange bias field shows a sudden switching off whereas the coercivity shows a sudden s…
A large magnetoresistance (MR) effect was observed in the layered compounds NdCoAsO and SmCoAsO, in which ferromagnetically ordered itinerant-electrons of Co are sandwiched by localized 4$f$-electrons of $Ln^{3+}$, below ferromagnetic-antiferromagnetic transition (FAFT) temperature $T_\mathrm{N}$ as observed in other FAFT compounds. In SmCoAsO, the large MR effect is also observed up to the Curie temperature $T_\mathrm{C}$, and it is found to be originating in the presence of another antiferromagnetic phase in the low-magnetic field region of the ferromagnetic phase.
Magnetic and heat capacity measurements have been carried out on the polycrystalline sample of DyNi which crystallizes in the orthorhombic FeB structure (space group Pnma). This compound is ferromagnetic with a Curie temperature of 59 K. Magnetization-field isotherms at low temperatures shows a step-like behavior characteristic of metamagnetic transitions. The magnetocaloric effect has been measured both in terms of isothermal magnetic entropy change and adiabatic temperature change for various applied magnetic fields. The maximum values of the entropy change and the temperature change are fou…
The Mössbauer Effect(ME) is frequently used to investigate magnetically ordered systems. One usually assumes that the magnetic order induces a hyperfine magnetic field, $B_{hyperfine}$, at the ME active site. This is the case in the ruthenates, where the temperature dependence of $B_{hyperfine}$ at $^{99}$Ru sites tracks the temperature dependence of the ferromagnetic or antiferromagnetic order. However this does not happen in the rare-earth intermetallics, GdRu$_2$ and HoRu$_2$. Specific heat, magnetization, magnetic susceptibility, Mössbauer effect, and neutron diffraction have been used to …
We report on the synthesis and physical properties of the new ternary intermetallic Ce$_2$Rh$_2$Ga. Its formation and dimorphism have been investigated by powder and single crystal X-ray diffractometry, as well as by differential thermal analyses. LT- and HT-Ce$_2$Rh$_2$Ga can be obtained by the chosen respective thermal treatment. The high-temperature form (HT-Ce$_2$Rh$_2$Ga), stable above 864(5)°C, is orthorhombic La2Ni3-type [Cmce, oS20, a=5.851(2) Å, b=9.618 (2) Å, c=7.487 (2) Å, V=421.3(2) Å3]; the low-temperature form (LT-Ce$_2$Rh$_2$Ga), stable below this temperature, is monoclinic Pr2C…
We present a detailed study of the dielectric and charge transport properties of the antiferromagnetic cubic spinel HgCr2S4. Similar to the findings in ferromagnetic CdCr2S4, the dielectric constant of HgCr2S4 becomes strongly enhanced in the region below 60 - 80 K, which can be ascribed to polar relaxational dynamics triggered by the onset of ferromagnetic correlations. In addition, the observation of polarization hysteresis curves indicates the development of ferroelectric order below about 70 K. Moreover, our investigations in external magnetic fields up to 5 T reveal the simultaneous occur…
A bulk diluted magnetic semiconductor (Sr,K)(Zn,Mn)$_{2}$As$_{2}$ was synthesized with decoupled charge and spin doping. It has a hexagonal CaAl$_{2}$Si$_{2}$-type structure with the (Zn,Mn)$_{2}$As$_{2}$ layer forming a honeycomb-like network. Magnetization measurements show that the sample undergoes a ferromagnetic transition with a Curie temperature of 12 K and \revision{magnetic moment reaches about 1.5 $μ_{B}$/Mn under $μ_0H$ = 5 T and $T$ = 2 K}. Surprisingly, a colossal negative magnetoresistance, defined as $[ρ(H)-ρ(0)]/ρ(0)$, up to $-$38\% under a low field of $μ_0H$ = 0.1 T and to $-…
We report the novel critical behavior of magnetization in low carrier concentration systems UTeS and USeS that exhibit the large negative magnetoresistance around the ferromagnetic transition temperatures T_C ~ 85 and 23 K, respectively. UTeS and USeS crystallize in the same orthorhombic TiNiSi-type crystal structure as those of uranium ferromagnetic superconductors URhGe and UCoGe. We determine the critical exponents, beta for the spontaneous magnetization M_s, gamma for the magnetic susceptibility chi, and delta for the magnetization isotherm at T_C with several methods. The ferromagnetic st…
We report a comprehensive investigation of the structural, magnetic, transport and thermodynamic properties of a single crystal PrAlSi, in comparison to its nonmagnetic analogue LaAlSi. PrAlSi exhibits a ferromagnetic transition at $T_C$ = 17.8 K which, however, is followed by two weak phase transitions at lower temperatures. Based on the combined dc and ac magnetic susceptibility measurements, we propose the two reentrant magnetic phases below $T_C$ to be spin glasses or ferromagnetic cluster glasses. When the magnetic glassy states are suppressed by small field, several remarkable features a…
Pr0.9Sr0.1CoO2.99 sample exhibits magnetoresistivity (MR) of up to 40 % at 5 K with a strong hysteresis/memory effect. Magnetisation measurements on Pr0.9Sr0.1CoO2.99 in an applied field of 100 Oe show that, as temperature decreases, the zero-field-cooled (ZFC) and field-cooled (FC) magnetisation curves branch clearly at 50 K, and a cusp appears in the ZFC branch at Tcusp 20 K. Magnetisation measurements in various fields between 100 and 10,000 Oe show that both the ZFC-FC branching temperature and, Tcusp, decrease with increasing field. The magnetization-field isotherms at 5 and 10 K show hys…
We report results of magnetization, zero field resistivity and magnetoresistance measurements in ferromagnetic Heusler alloy Co$_2$TiSn. There is a striking change in the character of electron transport as the system undergoes the paramagnetic to ferromagnetic transition. In the paramagnetic state the nature of the electron transport is like that of a semiconductor and this changes abruptly to metallic behaviour at the onset of ferromagnetic ordering. Application of external magnetic field tends to suppress this semiconducting like transport leading to a negative magnetoresistance which reache…
A heavy-mass electron state is realized in a doped valence bond solid (Ti1-xVx)2O3. In this system, itinerant holes mediate the mainly ferromagnetic RKKY interaction between the localized magnetic moments and become readily spin-polarized under a magnetic field, while showing large negative magnetoresistance. In spite of the ferromagnetic interaction among the carriers, their effective mass is found to be 1 or 2 orders of magnitude larger than that of usual doped semiconductors. Such strong mass renormalization is ascribable to the polaron formation on the Ti-dimer, where the spin-singlet stat…
First-principles calculations of the electronic structure of members of the $R$NiC$_2$ series are presented, and their Fermi surfaces investigated for nesting propensities which might be linked to the charge-density waves exhibited by certain members of the series ($R$ = Sm, Gd and Nd). Calculations of the generalized susceptibility, $χ_{0}({\bf q},ω)$, show strong peaks at the same ${\bf q}$-vector in both the real and imaginary parts for these compounds. Moreover, this peak occurs at a wavevector which is very close to that experimentally observed in SmNiC$_2$. In contrast, for LaNiC$_2$ (wh…
A ferromagnetic phase, characterized by electron carriers and a high temperature colossal magnetoresistance (HTCMR) dependent on the magnetic moment, and a semiconducting phase, characterized by hole carriers and a low temperature CMR (LTCMR), are observed in La$_{1-x}$Ca$_{x}$MnO$_3$ thin films by the van der Pauw method. The LTCMR is much more sensitive to the magnetic field than the HTCMR. In the ferromagnetic phase for films with anisotropic moments in two dimensions, a remnant resistivity of the order of 10$^{-8} \~Ωm$ is observed up to 100 K and increases exponentially with both a temper…
Transport and magnetic studies of Ca3Ru2O7 for temperatures ranging from 0.4 K to 56 K and magnetic fields, B, up to 45 T leads to strikingly different behavior when the field is applied along the different crystal axes. A ferromagnetic (FM) state with full spin polarization is achieved for B||a-axis, but colossal magnetoresistance is realized only for B||b-axis. For B||c-axis, Shubnikov-de Haas oscillations are observed and followed by a less resistive state than for B||a. Hence, in contrast to standard colossal magnetoresistive materials, the FM phase is the least favorable for electron hopp…
We develop a variational mean-field theory of the ferromagnetic transition in compounds like Lanthanum-Manganite within the framework of the Double-Exchange Model supplemented by modest disorder. We obtain analytical expressions for the transition temperature, its variation with the valence electron-density and its decrease with disorder. We derive an expression for the conductivity for both the paramagnetic and the ferromangetic metallic phases, and study its dependence on the temperature and magnetic field. A simple relation between the resistivity in the ferromagnetic phase and the spontane…
In the series R2PdSi3, Nd2PdSi3 is an anomalous compound in the sense that it exhibits ferromagnetic order unlike other members in this family. The magnetic ordering temperature is also unusually high compared to the expected value for a Nd-based system, assuming 4f localization. Here, we have studied the electronic structure of single crystalline Nd2PdSi3 employing high resolution photoemission spectroscopy and ab initio band structure calculations. Theoretical results obtained for the effective electron correlation strength of 6 eV corroborate well with the experimental valence band spectra.…
In the present work, a relation has been established between degree of polarization and effective mass ratio (EMR) and magnetoresistance (MR) of one-dimensional non-degenerate system (which can represent a nano-wire or a linear chain of atoms and molecules in one dimension) by using a non-degenerate Hubbard model, which includes diagonal and off-diagonal matrix elements of Coulomb interaction. EMR is one of the most important property, which provides information that how much itinerant the system is? Within the mean field approximation, it is found that, due to the presence of off-diagonal ele…
Recognising the difficulties in systematic understanding of the physical characteristics of strongly correlated f-electron systems, we considered it worthwhile to subject the so-called "normal" f-electron systems like those of Gd to careful investigations. We find that the spin-disorder contribution to electrical resistivity ($ρ$) in the paramagnetic state, instead of remaining contant, surprisingly increases with decreasing temperature (T) in the paramagnetic state in some of the Gd alloys. In some cases, this "excess resistance" is so large that a distinct minimum in the plot of $ρ$ versus T…
In the family of double perovskites, colossal magnetoresistance (CMR) has been so far observed only in half-metallic ferrimagnets such as the known case Sr$_2$FeMoO$_6$ where it has been assigned to the tunneling MR at grain boundaries due to the half-metallic nature. Here we report a new material-Tl$_2$NiMnO$_6$, a relatively ordered double perovskite stablized by the high pressure and high temperature synthesis-showing CMR in the vicinity of its Curie temperature. We explain the origin of such effect with neutron diffraction experiment and electronic structure calculations that reveal the ma…
Magnetic phases for the intermetallic compound NdMn1.4Co0.6Si2 have been investigated at various temperatures by dc magnetization, neutron diffraction and neutron depolarization. Our study shows multiple magnetic phase transitions with temperature (T) over 1.5-300 K. In agreement with dc-magnetization and neutron depolarization results, the temperature dependence of the neutron diffraction patterns shows five distinct regions with different magnetic phases. These temperature regions are (i) T >= 215 K, (ii) 215 K > T >= 50 K, (iii) 50 K > T >= 40 K, (iv) 40 K > T > 15 K, and (v) T =< 15 K. The…
We report the magnetic properties strongly varying with the rare-earth elements in the newly found ternary compounds $R$Al$_{0.9}$Si$_{1.1}$, which crystallize in the tetragonal $α$-ThSi$_2$-type structure. For $R$ = Ce the alloy has a weak ferromagnetism below 11 K and for $R$ = Pr it orders ferromagnetically at 17 K, while for $R$ = Gd it is antiferromagnetic with $T_{\rm N}$ = 30.5 K. In addition, we find no field effect on $T_{\rm N}$ of $R$ = Gd because of the large internal mean field, but significant changes in the magnetic properties of $R$ = Ce and Pr.
In this study, we present a theoretical interpretation of the experimental results that the anisotropic magnetoresistance (AMR) effect has a four-fold symmetric component, $c_4$, in cubic ferromagnetic metals. The theoretical model that we employ is based on the Anderson impurity model that includes a four-fold symmetric crystalline electric field, and we assume that the impurities have 3d electron orbitals and spin--orbit interaction (SOI). We describe the DC conductivity on the basis of the Kubo formula, and we investigate $c_4$ by analyzing the magnetization direction dependence of the resu…
We report the effect of Ga substitution on magnetization, magnetoresistance, and magnetostriction in polycrystalline Pr0.6Sr0.4Co1-yGayO3 (y=0.0-0.3) samples. Upon substitution of the non-magnetic Ga3+ cation for magnetic Co3+, the low-temperature ground state transforms from ferromagnetic metallic for y = 0 to cluster glass semiconductor for y = 0.2. Magnetoresistance at 7T is negative and its magnitude increases from 2 percentage for y = 0 to 30 percentage for y = 0.3 at 10 K. On the other hand, magnetostriction at 10 K is positive and its value decreases with increasing y. Interestingly, th…
Studies on the phenomenon of magnetoresistance (MR) have produced intriguing and application-oriented outcomes for decades--colossal MR, giant MR and recently discovered extremely large MR of millions of percents in semimetals can be taken as examples. We report here the investigation of oscillating MR in a cubic intermetallic compound GdPd$_3$, which is the only compound that exhibits MR oscillations between positive and negative values. Our study shows that a very strong correlation between magnetic, electrical and magnetotransport properties is present in this compound. The magnetic structu…
The n-type HgCr2Se4 exhibits a sharp semiconductor-to-metal transition (SMT) in resistivity accompanying the ferromagnetic order at TC = 106 K. Here, we investigate the effects of pressure and magnetic field on the concomitant SMT and ferromagnetic order by measuring resistivity, dc and ac magnetic susceptibility, as well as single-crystal neutron diffraction under various pressures up to 8 GPa and magnetic fields up to 8 T. Our results demonstrate that the ferromagnetic metallic ground state of n-type HgCr2Se4 is destabilized and gradually replaced by an antiferromagnetic, most likely a spira…
Systematic experimental (vibrating sample magnetometry) and theoretical (electronic structure calculations using charge and spin self-consistent Korringa-Kohn-Rostoker Green function method) studies were performed on a series of intermetallic sigma-phase Fe(100-x)Re(x) (x = 43-53) compounds. Clear evidence was found that all investigated samples exhibit magnetism with an ordering temperature ranging between 65 K for x = 43 and 23 K for x = 53. The magnetism was revealed to be itinerant and identified as a spin-glass (SG) possibly having a re-entrant character. The SG was found to be heterogene…
We investigate the dc electric response induced by ferromagnetic resonance in ferromagnetic Permalloy (Ni80Fe20) microstrips. The resulting magnetization precession alters the angle of the magnetization with respect to both dc and rf current. Consequently the time averaged anisotropic magnetoresistance (AMR) changes (photoresistance). At the same time the time-dependent AMR oscillation rectifies a part of the rf current and induces a dc voltage (photovoltage). A phenomenological approach to magnetoresistance is used to describe the distinct characteristics of the photoresistance and photovolta…
We have performed a systematic investigation of the longitudinal and transverse magnetoresistance of a single ferromagnetic domain in (Ga,Mn)As. We find that, by taking into account the intrinsic dependence of the resistivity on the magnetic induction, an excellent agreement between experimental results and theoretical expectations is obtained. Our findings provide a detailed and fully quantitative validation of the theoretical description of magnetotransport through a single ferromagnetic domain. Our analysis furthermore indicates the relevance of magneto-impurity scattering as a mechanism fo…
The phenomena of odd-parity magnetoresistance and the planar Hall effect are deeply entwined with ferromagnetism. The intrinsic magnetization of the ordered state permits these unusual and rarely observed manifestations of Onsager's theorem when time reversal symmetry is broken at zero applied field. Here we study two classes of ferromagnetic materials, rare-earth magnets with high intrinsic coercivity and antiferromagnetic pyrochlores with strongly-pinned ferromagnetic layers at domain walls, which both exhibit odd-parity magnetoresistive behavior. The peculiar angular variation of the respon…
We performed a systematic study of the temperature- and field-dependence of magnetization and resistivity of Gd2PdSi3, which is a centrosymmetric skyrmion crystal. While the magnetization behavior is consistent with the reported phase diagram based on susceptibility, we show that a phase diagram can also be constructed based on the anomalous magnetoresistance with one-to-one correspondence among all the features. In addition, the crossover boundary into the field-induced ferromagnetic state is also identified. Our results suggest that the ferromagnetic spin fluctuations above the Néel temperat…
We report on the physical properties of single crystalline EuRhSi$_3$ and polycrystalline EuIrSi$_3$, inferred from magnetisation, electrical transport, heat capacity and $^{151}$Eu Mössbauer spectroscopy. These previously known compounds crystallise in the tetragonal BaNiSn$_3$-type structure. The single crystal magnetisation in EuRhSi$_3$ has a strongly anisotropic behaviour at 2 K with a spin-flop field of 13 T, and we present a model of these magnetic properties which allows the exchange constants to be determined. In both compounds, specific heat shows the presence of a cascade of two clo…
UCoGa and URhGa, two isostructural compounds show opposite signs of the initial response of Curie temperature to applied hydrostatic premenssure. To determine the physical origin of this contradiction the magnetization data measured with respect to temperature, magnetic field and hydrostatic pressure were analyzed in the framework of the Takahashi's spin-fluctuation theory. The parameters T0 and TA characterizing the distribution widths of the spin-fluctuation spectrum in the energy and wave vector space, respectively, and TC/T0, the degree of the 5f-electron localization have been determined.…
Critical phenomena of ferromagnetic transition in colossal magnetoresistance manganites are theoretically studied. Concerning the critical exponents for this transition, there still remains controversy among experimental results. In order to clarify intrinsic physics of the manganites through a comparison with theoretical prediction, we investigate the critical phenomena of double-exchange models by using finite-size scaling analysis on unbiased numerical results. As a result, we show that the critical exponents of the ferromagnetic transition of the three-dimensional double-exchange model is …
The coupling of magnetic and electronic degrees of freedom to the crystal lattice in the ferromagnetic semimetal EuB$_6$, which exhibits a complex ferromagnetic order and a colossal magnetoresistance (CMR) effect, %, very likely involving magnetic polarons, is studied by high-resolution thermal expansion and magnetostriction experiments. EuB$_6$ may be viewed as a model system, where pure magnetism-tuned transport and the response of the crystal lattice can be studied in a comparatively simple environment,i.e., not influenced by strong crystal-electric field effects and Jahn-Teller distortions…
We argue that the extension of the BCS theory to the strong-coupling regime describes the high-temperature superconductivity of cuprates and the colossal magnetoresistance (CMR) of ferromagnetic oxides if the phonon dressing of carriers and strong attractive correlations are taken into account. The long-range Froehlich electron-phonon interaction has been identified as the most essential in cuprates providing "superlight" lattice polarons and bipolarons. Here some kinetic, magnetic, and more recent thermomagnetic normal state measurements are interpreted in the framework of the strong-coupling…
We present a small-but-sizeable magnetic polaron picture where transport at high temperatures is activated while at low temperatures it is band-like. We show that both double exchange and finite bandwidth effects are important to understand colossal magnetoresistance as well as the coincidence of the metal-insulator and the ferromagnetic transitions in manganites. The magnetic transition is explained using band-like motion of the polarons.
A two-staged, uniaxial magnetoresistive effect has been discovered in SrCo6O11 having a layered hexagonal structure. Conduction electrons and localized Ising spins are in different sublattices but their interpenetration makes the conduction electrons sensitively pick up the stepwise field-dependence of magnetization. The stepwise field-dependence suggests two competitive interlayer interactions between ferromagnetic Ising-spin layers, i.e., a ferromagnetic nearest-layer interaction and an antiferromagnetic next-nearest-layer interaction. This oxide offers a unique opportunity to study nontrivi…
We report a complete multicomponent mean-field-theory for the coexistence and competition of charge ordering (CO), antiferromagnetic (AFM) and ferromagnetic (FM) spin ordering in the presence of a uniform magnetic field. Doping the AFM or CO state always generates a ferromagnetic component. Itinerant FM, AFM and CO, necessarily coexist and compete in a particle-hole asymmetric system. Melting of large AFM-CO orders by small magnetic fields and the related phenomenon of Colossal Magnetoresistance (CMR) may arise whenever the CO and AFM order parameters have similar magnitude and momentum struct…