Epitaxial thin films of LaCoO_{3} (E-LCO) exhibit ferromagnetic order with a transition temperature T_c = 85 K, while polycrystalline thin LaCoO_{3} films (P-LCO) remain paramagnetic. The temperature-dependent spin-state structure for both E-LCO and P-LCO was studied by x-ray absorption spectroscopy at the Co L_{2,3} and O K edges. Considerable spectral redistributions over temperature are observed for P-LCO. The spectra for E-LCO, on the other hand, do not show any significant changes for temperatures between 30 K and 450 K at both edges, indicating that the spin state remains constant and that the epitaxial strain inhibits any population of the low-spin (S = 0) state with decreasing temperature. This observation identifies an important prerequisite for ferromagnetism in E-LCO thin films.
The enigma of the emergent ferromagnetic state in tensile-strained LaCoO3 thin films remains to be explored because of the lack of a well agreed explanation. The direct magnetic imaging technique using a low-temperature magnetic force microscope (MFM) is critical to reveal new aspects of the ferromagnetism by investigating the lateral magnetic phase distribution. Here we show the experimental demonstration of the rare halved occupation of the ferromagnetic state in tensile-strained LaCoO3 thin films on SrTiO3 substrates using the MFM. The films have uniformly strained lattice structure and min…
With local density approximation + Hubbard $U$ (LDA+$U$) calculations, we show that the ferromagnetic (FM) insulating state observed in tensile-strained LaCoO$_3$ epitaxial thin films is most likely a mixture of low-spin (LS) and high-spin (HS) Co, namely, a HS/LS mixture state. Compared with other FM states, including the intermediate-spin (IS) state (\textit{metallic} within LDA+$U$), which consists of IS Co only, and the insulating IS/LS mixture state, the HS/LS state is the most favorable one. The FM order in HS/LS state is stabilized via the superexchange interactions between adjacent LS …
Ferromagnetic insulators play a crucial role in the development of low-dissipation quantum magnetic devices for spintronics. Epitaxial LaCoO3 thin film is a prominent ferromagnetic insulator, in which the robust ferromagnetic ordering emerges owing to epitaxial strain. Whereas it is evident that strong spin-lattice coupling induces ferromagnetism, the reported ferromagnetic properties of epitaxially strained LaCoO3 thin films were highly consistent. For example, even under largely modulated degree of strain, the reported Curie temperatures of epitaxially strained LaCoO3 thin films lie within 8…
Reversible and irreversible discontinuities at around 573 K and 823 K in the electric conductivity of a strained 175 nm thin film of (La0.8Sr0.2)0.95Ni0.2Fe0.8O3-δ grown by pulsed laser deposition on SrTiO3 (110) are reflected by valence band changes as monitored in photoemission and oxygen K-edge x-ray absorption spectra. The irreversible jump at 823 K is attributed to depletion of doped electron holes and reduction of Fe4+ to Fe3+, as evidenced by oxygen and iron core level soft x-ray spectroscopy, and possibly of a chemical origin, whereas the reversible jump at 573 K possibly originates fr…
Dedicated control of oxygen vacancies is an important route to functionalizing complex oxide films. It is well-known that tensile strain significantly lowers the oxygen vacancy formation energy, whereas compressive strain plays a minor role. Thus, atomically reconstruction by extracting oxygen from a compressive-strained film is challenging. Here we report an unexpected LaCoO2.5 phase with a zigzag-like oxygen vacancy ordering through annealing a compressive-strained LaCoO3 in vacuum. The synergetic tilt and distortion of CoO5 square pyramids with large La and Co shifts are quantified using sc…
We study ferromagnetic ordering and microscopic inhomogeneity in tensile strained LaCoO$_3$ using numerical simulations. We argue that both phenomena originate from effective superexchange interactions between atoms in the high-spin (HS) state mediated by the intermediate-spin excitations. We derive a model of the HS excitation as a bare atomic state dressed by electron and electron-hole fluctuations on the neighbor atoms. We construct a series of approximations to account for electron correlation effects responsible for HS fluctuations and magnetic exchange. The obtained amplitudes and direct…
A quantitative mathematical model for the critical thickness of strained epitaxial metal films is presented, at which the magnetic moment experiences a reorientation from in-plane to perpendicular magnetic anisotropy. The model is based on the minimum of the magnetic anisotropy energy with respect to the orientation of the magnetic moment of the film. Magnetic anisotropy energies are taken as the sum of shape anisotropy, magnetocrystalline anisotropy and magnetoelastic anisotropy, the two latter ones being present as constant surface and variable volume contributions. Other than anisotropy mat…
Epitaxially strained LaCoO3 (LCO) thin films were grown with different film thickness, t, on (001) oriented (LaAlO3)0.3(SrAl0.5Ta0.5O3)0.7 (LSAT) substrates. After initial pseudomorphic growth the films start to relieve their strain partly by the formation of periodic nano-twins with twin planes predominantly along the <100> direction. Nano-twinning occurs already at the initial stage of growth, albeit in a more moderate way. Pseudomorphic grains, on the other hand, still grow up to a thickness of at least several tenths of nanometers. The twinning is attributed to the symmetry lowering of the…
Multiferroics with the coexistence of ferroelectric and ferromagnetic orders are ideal candidates for magnetoelectric applications. Unfortunately, only very few ferroelectric-ferromagnetic multiferroics (with low magnetic critical temperature) were discovered. Here we perform first principles calculations to investigate the effects of the epitaxial strain on the properties of BiMnO3 films grown along the pseudocubic [001] direction. Unlike the ground state with the centrosymmetric C2/c space group in bulk, we reveal that the tensile epitaxial strain stabilizes the ferromagnetic and ferroelectr…
First-principles calculations reveal a large cooperative coupling of Jahn-Teller (JT) distortion to oxygen-octahedron rotations in perovskite LaMnO$_3$. The combination of the two distortions is responsible for stabilizing the strongly orthorhombic $A$-AFM insulating ($I$) $Pbnm$ ground state relative to a metallic ferromagnetic (FM-$M$) phase. However, epitaxial strain due to coherent matching to a crystalline substrate can change the relative stability of the two states. In particular, coherent matching to a square-lattice substrate favors the less orthorhombic FM-$M$ phase, with the $A$-AFM…
We use density-functional theory with the local-density approximation to study the structural and ferroelectric properties of SrTiO$_3$ under misfit strains. Both the antiferrodistortive (AFD) and ferroelectric (FE) instabilities are considered. The rotation of the oxygen octahedra and the movement of the atoms are fully relaxed within the constraint of a fixed in-plane lattice constant. We find a rich misfit strain-induced phase transition sequence and is obtained only when the AFD distortion is taken into account. We also find that compressive misfit strains induce ferroelectricity in the te…
Motivated by the puzzling report of the observation of a ferromagnetic insulating state in LaMnO$_3$/SrTiO$_3$ heterostructures, we calculate the electronic and magnetic state of LaMnO$_3$, coherently matched to a SrTiO$_3$ square substrate within a "strained-bulk" geometry. We employ three different density functional theory based computational approaches: (a) density functional theory (DFT) supplemented with Hubbard U (DFT+U), (b) DFT + dynamical mean field theory (DMFT), and (c) a hybrid functional treatment of the exchange-correlation functional. While the first two approaches include loca…
The effect of epitaxial strain on the structural and electronic properties of LaVO_3 is investigated through density functional theory (DFT) and dynamical mean field theory (DMFT). Two different growth orientations of the crystal are considered, one preserving the bulk Pbnm space-group symmetry and another giving rise to a symmetry lowering to P2_1/m. In the nonmagnetic DFT structures, the two growth orientations are equally favored for all tensile strains considered here, as well as for compressive strains weaker than -3%. For stronger compressive strains, the P2_1/m orientation is favored an…
Magneto-transport properties of SrIrO$_3$ thin films epitaxially grown on SrTiO$_3$, using reactive RF sputtering, are investigated. A large anisotropy between the in-plane and the out-of-plane resistivities is found, as well as a signature of the substrate cubic to tetragonal transition. Both observations result from the structural distortion associated to the epitaxial strain. The low-temperature and field dependences of the Hall number are interpreted as due to the contribution of Coulomb interactions to weak localization, evidencing the strong correlations in this material. The introductio…
Observation of mirror-odd and mirror-even spin texture in ultrathin epitaxially strained RuO2 films
University of Minnesota-Twin Cities（明尼苏达大学双城分校）；Kyung Hee University（庆熙大学）；Rice University（莱斯大学）；Paul Scherrer Institute（保罗谢勒研究所）；Gwangju Institute of Science and Technology (GIST)（光州科学技术院）
Electronic structure and magnetic correlations in the epitaxially strained bilayer nickelate La$_3$Ni$_2$O$_{7}$
M. N. Mikheev Institute of Metal Physics, Russian Academy of Sciences（俄罗斯科学院 M.N. 米凯耶夫金属物理研究所）；Institute of Physics and Technology, Ural Federal University（乌拉尔联邦大学物理与技术学院）
Epitaxial strain imposed in complex oxide thin films by heteroepitaxy is recognized as a powerful tool for identifying new properties and exploring the vast potential of materials performance. A particular example is LaCoO3, a zero spin, nonmagnetic material in the bulk, whose strong ferromagnetism in a thin film remains enigmatic despite a decade of intense research. Here, we use scanning transmission electron microscopy complemented by X-ray and optical spectroscopy to study LaCoO3 epitaxial thin films under different strain states. We observed an unconventional strain relaxation behavior re…
Epitaxially strained SrRuO3 films have been a model system for understanding the magnetic anisotropy in metallic oxides. In this paper, we investigate the anisotropy of the Ru 4d and O 2p electronic structure and magnetic properties using high-quality epitaxially strained (compressive and tensile) SrRuO3 films grown by machine-learning-assisted molecular beam epitaxy. The element-specific magnetic properties and the hybridization between the Ru 4d and O 2p orbitals were characterized by Ru M2,3-edge and O K-edge soft X-ray absorption spectroscopy and X-ray magnetic circular dichroism measureme…
Transition metal oxides possess complex free energy surfaces with competing degrees of freedom. Photoexcitation allows shaping of such rich energy landscapes. In epitaxially strained $\mathrm{La_{0.67}Ca_{0.33}MnO_3}$, optical excitation with a sub-100 fs pulse above $2\ \mathrm{mJ/cm^2}$ leads to a persistent metallic phase below 100 K. Using single-shot optical and terahertz spectroscopy, we show that this phase transition is a multi-step process. We conclude that the phase transition is driven by partial charge order melting, followed by growth of the persistent metallic phase on longer tim…
Manipulating the orbital occupation of valence electrons via epitaxial strain in an effort to induce new functional properties requires considerations of how changes in the local bonding environment affect the band structure at the Fermi level. Using synchrotron radiation to measure the x-ray linear dichroism of epitaxially strained films of the correlated oxide CaFeO3, we demonstrate that the orbital polarization of the Fe valence electrons is opposite from conventional understanding. Although the energetic ordering of the Fe 3d orbitals is confirmed by multiplet ligand field theory analysis …
We have used polarized Raman scattering to probe lattice vibrations and charge ordering in 12 nm thick, epitaxially strained PrNiO$_3$ films, and in superlattices of PrNiO$_3$ with the band-insulator PrAlO$_3$. A carefully adjusted confocal geometry was used to eliminate the substrate contribution to the Raman spectra. In films and superlattices under tensile strain, which undergo a metal-insulator transition upon cooling, the Raman spectra reveal phonon modes characteristic of charge ordering. These anomalous phonons do not appear in compressively strained films, which remain metallic at all …
We report a comparative study of the properties of very thin films of La0.67Ca0.33MnO3 grown epitaxially under strain on flat SrTiO3 (STO) and on 1 deg miscut STO. For the films on flat STO the transport properties show well-known behavior, namely values of the metal-insulator transition temperature which are strongly reduced with respect to the bulk value. The reduction in films on miscut STO is significantly less strong than in films on flat STO, even though they appear similar as to strain state. Moreover, the residual resistance at low temperatures is lower than for the case of flat films.…
While structure refinement is routinely achieved for simple bulk materials, the accurate structural determination still poses challenges for thin films due on the one hand to the small amount of material deposited on the thicker substrate and, on the other hand, to the intricate epitaxial relationships that substantially complicate standard X-ray diffraction analysis. Using a combined approach, we analyze the crystal structure of epitaxial LaVO$_3$ thin films grown on (100)-oriented SrTiO$_3$. Transmission electron microscopy study reveals that the thin films are epitaxially grown on SrTiO$_3$…
The correlated oxide SmNiO3 (SNO) exhibits an insulator to metal transition (MIT) at 130 °C in bulk form. We report on synthesis and electron transport in SNO films deposited on LaAlO3 (LAO) and Si single crystals. X-ray diffraction studies show that compressively strained single-phase SNO grows epitaxially on LAO while on Si, mixed oxide phases are observed. MIT is observed in resistance-temperature measurements in films grown on both substrates, with charge transport in-plane for LAO/SNO films and out-of-plane for Si/SNO films. Electrically-driven memristive behavior is realized in LAO/SNO f…
B-site ordered thin films of double perovskite Sr$_2$CoIrO$_6$ were epitaxially grown by a metal-organic aerosol deposition technique on various substrates, actuating different strain states. X-ray diffraction, transmission electron microscopy and polarized far-field Raman spectroscopy confirm the strained epitaxial growth on all used substrates. Polarization dependent Co $L_{2,3}$ X-ray absorption spectroscopy reveals a change of the magnetic easy axis of the antiferromagnetically ordered (high-spin) Co$^{3+}$ sublattice within the strain series. By reversing the applied strain direction from…
We report x-ray resonant magnetic scattering (XRMS) and resonant inelastic x-ray scattering (RIXS) studies of epitaxially-strained $\mathrm{Sr_2IrO_4}$ thin films. The films were grown on $\mathrm{SrTiO_3}$ and $\mathrm{(LaAlO_3)_{0.3}(Sr_2AlTaO_6)_{0.7}}$ substrates, under slight tensile and compressive strains, respectively. Although the films develop a magnetic structure reminiscent of bulk $\mathrm{Sr_2IrO_4}$, the magnetic correlations are extremely anisotropic, with in-plane correlation lengths significantly longer than the out-of-plane correlation lengths. In addition, the compressive (…
Magneto optic measurements are a very powerful tool for investigating the polarization of a conduction band as a function of temperature and are used here to study the polarization of the mobile electrons in 50nm LSMO (x=0.3) strained thin films grown epitaxially on single crystalline (001) LaAlO3 (LAO) and (001) lattice matched substrate (LSAT). The magnetic circular dichroism (MCD) has been investigated in magnetic fields up to 0.5 T and over a temperature range (10 to 450 K). The MCD spectra of both the films show a peak at the band gap at around 3 eV and the peak is found to be shifted tow…
5d iridates have shown vast emergent phenomena due to a strong interplay among its lattice, charge and spin degrees of freedom, because of which the potential in spintronic application of the thin-film form is highly leveraged. Here we have epitaxially stabilized perovskite SrIr$_{0.8}$Sn$_{0.2}$O$_3$ on [001] SrTiO$_3$ substrates through pulsed laser deposition and systematically characterized the structural, electronic and magnetic properties. Physical properties measurements unravel an insulating ground state with a weak ferromagnetism in the compressively strained epitaxial film. The octah…