arXiv 0807.30982008-07-19cond-mat.supr-con

Effect of doping on irreversible Campbell length in MgB$_2$ single crystals

C. Martin, M. D. Vannette, R. T. Gordon, R. Prozorov, J. Karpinski, N. D. Zhigadlo

发表信息：: Phys. Rev. B 78, 144512 (2008)
DOI：: 10.1103/PhysRevB.78.144512

英文摘要：

We have measured small-amplitude rf penetration depth $λ(H,T)$ in pure and C, Li and (Li+C) doped single crystals of MgB$_2$. The effect of doping on the critical temperature T$_c$ and on the upper critical field H$_{c2}$ was found to be in good agreement with previous results. We report the presence of clear signatures of irreversibility in $λ(H,T)$, associated with the peak effect. Carbon doping enhances the signature and shifts its position on the H-T phase diagram to higher temperatures. Contrary to this, Li substitution has the effect of suppressing the peak effect to lower temperatures. Analysis of both zero field (ZFC) and field cooled (FC) measurements suggests that the hysteresis associated with the peak effect is due to macroscopic screening supercurrents, $j$, generated during the magnetic field ramp.

机构、总结、中文摘要均由AI分析而来，可能存在错误，请以论文正文为准。

阅读原文

阅读 PDF ↗

arXiv 页面 ↗HTML 原文 ↗

本文内容

英文摘要相关论文

机构、总结、中文摘要均由AI分析而来，可能存在错误，请以论文正文为准。

继续探索

相关论文

Flux dynamics and vortex phase diagram of the new superconductor $MgB_2$

Magnetic critical current density and relaxation rate have been measured on $MgB_2$ bulks from 1.6 K to $T_c$ at magnetic fields up to 8 Tesla. A vortex phase diagram is depicted based on these measurement. Two phase boundaries $H_{irr}^{bulk}(T)$ and $H_{irr}^{g}(T)$ characterizing different irreversible flux motions are found. The $H_{irr}^{bulk}(T)$ is characterized by the appearance of the linear resistivity and is attributed to quantum vortex melting induced by quantum fluctuation of vortices in the rather clean system. The second boundary $ H_{irr}^g(T) $ reflects the irreversible flux m…

2001-03-26cond-mat.supr-con

Disorder-induced Phase Transition of Vortex Matter in MgB2

Measurements of single crystalline MgB2 with torque magnetometry in fields up to 90 kOe reveal a sharp peak in the irreversible torque at about 0.85 Hc2. In the region between peak onset and maximum, pronounced history effects occur. Angle and temperature dependence of the characteristic peak fields track those of Hc2. The features observed suggest that the peak marks a disorder-induced phase transition of vortex matter between a quasi-ordered Bragg glass and a highly-disordered glass.

2002-11-01cond-mat.supr-con

Prominent bulk pinning effect in the MgB_2 superconductor

We report the magnetic-field dependence of the irreversible magnetization of the recently discovered binary superconductor MgB$_{2}$. For the temperature region of $T< 0.9T_c$, the contribution of the bulk pinning to the magnetization overwhelms that of the surface pinning. This was evident from the fact that the magnetization curves, $M(H)$, were well described by the critical-state model without considering the surface pinning effect. It was also found that the $M(H)$ curves at various temperatures scaled when the field and the magnetization were normalized by the characteristic scaling fact…

2001-04-12cond-mat.supr-con

Comment on "Superconducting anisotropy and evidence for intrinsic pinning in single crystalline MgB2"

In a recent paper [Phys. Rev. B 66, 012501 (2002)], torque data measured on a MgB2 single crystal in fields from 10 to 60 kOe at 10 K were presented. The authors obtained the anisotropy gamma by fitting a theoretical expression to the data and concluded that the anisotropy is field independent gamma \approx 4.3. They also reported the observation of "intrinsic pinning", which they take as experimental evidence for the occurence of superconductivity in the boron layers. In this comment, we discuss the range of validity of the theoretical expression used by the authors and show that the conclusi…

2002-06-21cond-mat.supr-con

Strongly enhancend anisotropic upper critical field in carbon substituted MgB2: impact of Fermi surface changes

The upper critical field Hc2||c(0) of 85 kOe in Mg(B0.94C0.06)2 single crystals, determined from torque measurements, is more than twice as large as that one of 31 kOe in unsubstituted MgB2. Anisotropy of Hc2 increases from about 3.4 near Tc, the value close to that in MgB2, to about 4 at low temperature, the value considerably lower than that in MgB2. The corresponding Hc2||ab(0) of about 330-350 kOe is likely close to the maximum enhancement due to C substitution. The position of a sharp peak in the irreversible torque Hmax was found to be shifted to lower reduced fields H/Hc2 in comparison …

2004-04-23cond-mat.supr-con

High-pressure synthesis of MgB2 with addition of Ti

The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2 at 33 K in 0 T field and at 20 K up to 3 T. At 20 K the critical current density higher than 10 kA/cm^2 was observed up to 5 T field. In the magnetic field up to 2 T high-pressure synthesized MgB2 (with 10 % of Ti) at 20 K behaves in the same manner as Nb3Sn at 4.2 K. In XRD patterns of magnesium diboride with the Ti added, we observed no evidence of titanium…

2003-06-01cond-mat.mtrl-scicond-mat.supr-con

更多相关论文收起更多论文

Two band superconductivity in MgB2: basic anisotropic properties and phase diagram

Magnesium diboride MgB2 has been an extraordinarily hot research topic since the discovery of superconductivity below 40 K, due to the vast amount of unusual properties originating from the involvement in superconductivity of two sets of bands that are of a different dimensionality. We review, with a strong focus on results obtained by torque magnetometry, how this leads to a complex behavior of the anisotropic superconducting state properties. The different dimensionality of the two sets of bands is manifested in the upper critical field Hc2 anisotropy, which was found to strongly decrease wi…

2003-05-04cond-mat.supr-con

Conventional superconductivity and hysteretic Campbell penetration depth in single crystals MgCNi$_3$

Single crystals of MgCNi$_3$, with areas sized up to 1 mm$^{2}$, were grown by the self flux method using a cubic anvil high pressure technique. The first critical field \textit{H$_{c1}$}, determined from a zero temperature extrapolation, is around 18 mT. Using the tunnel - diode resonator technique, the London penetration depth was measured with no applied \textit{dc} field and the Campbell penetration depth was measured with the external \textit{dc} fields up to 9T for two different sample orientations with respect to the direction of applied magnetic field. The absolute value of the London …

2013-02-20cond-mat.supr-con

Growth of c-oriented MgB2 thin films by Pulsed Laser Deposition: structural characterization and electronic anisotropy

MgB2 thin films were deposited using Pulsed Laser Deposition (PLD) and ex-situ annealing in Mg atmosphere. The films presented critical temperatures up to 36K and turned out to be preferentially c-oriented both on Al2O3 (r-cut) and MgO(100) substrates. Synchrotron analyses gave also some indications of in plane texturing. The films exhibit very fine grain size (1200angstromin the basal plane and 100angstrom along c-axis) but the general resistivity behavior and the remarkable extension of the irreversible region confirm that the grains boundaries are not barriers for supercurrents. Upper criti…

2001-07-02cond-mat.supr-con

Superconducting screening on different length scales in high-quality bulk MgB2 superconductor

High quality bulk MgB2 exhibit a structure of voids and agglomeration of crystals on different length-scales. Because of this, the superconducting currents percolate between the voids in the ensuing structure. Magnetic measurements reveal that the superconducting currents circulate on at least three different length-scales, of ~1 micrometre, ~10 micrometre and whole of the sample (~millimetre). Each of these screenings contributes to the measured irreversible magnetic moment (Dm). The analysis of the field dependence of Dm for samples of subsequently decreasing size showed that the critical cu…

2004-02-13cond-mat.supr-con

Effect of nanometer-sized B powder on phase formation of polycrystalline MgB2

The size effect of the raw B powder on the MgB2 phase formation has been studied by the technique of in-situ high temperature resistivity (HT-rT) measurement. The onset temperature, Tonset, and the completion temperature, TPF, of the phase formation are determined directly during the ongoing thermal process. These two temperatures, Tonset and TPF of the sample synthesized using nanometer B and Mg powders (NanoB-MgB2) are 440 C and 490 C, respectively, the same as those of the sample using micrometer B and nanometer Mg powders (MicroB-MgB2). This indicates that the phase formation temperature o…

2004-10-21cond-mat.mtrl-scicond-mat.supr-con

Effects of high pressure on the physical properties of MgB2

The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and mechanical characteristics: critical current densities of 1.8-1.0 \cdot 106 A/cm2 in the self field and 103 A/cm2 in a magnetic field of 8 T at 20 K, 5-3 \cdot 105 A/cm2 in self field at 30 K, the corresponding critical fields being HC2 = 15 T at 22 K and irreversible fields Hirr =13 T at 20 K, and Hirr =3.5 T at 30 K, thermal conduction of 53+/-2 W/(m \cdot κ), th…

2010-05-12cond-mat.supr-con

Doping dependent Irreversible Magnetic Properties of Ba(Fe1-xCox)2As2 Single Crystals

We discuss the irreversible magnetic properties of self-flux grown Ba(Fe1-xCox)2As2 single crystals for a wide range of concentrations covering the whole phase diagram from the underdoped to the overdoped regime, x=0.038, 0.047, 0.058, 0.071, 0.074, 0.10, 0.106 and 0.118. Samples were characterized by a magneto-optical method and show excellent spatial uniformity of the superconducting state. The overall behavior closely follows classical Bean model of the critical state. The field-dependent magnetization exhibits second peak at a temperature and doping - dependent magnetic field, Hp. The evol…

2009-02-02cond-mat.supr-con

Field-induced suppression of the pi-band superconductivity and magnetic hysteresis in the microwave surface resistance of MgB_2 at temperatures near T_c

We report on the magnetic-field-induced variations of the microwave surface resistance, R_s, in a polycrystalline MgB_2 sample, at different values of temperature. We have detected a magnetic hysteresis in R_s, which exhibits an unexpected plateau on decreasing the DC magnetic field below a certain value. In particular, at temperatures near T_c the hysteresis manifests itself only through the presence of the plateau. Although we do not quantitatively justify the anomalous shape of the magnetic hysteresis, we show that the results obtained in the reversible region of the R_s(H) curve can be qui…

2009-03-12cond-mat.supr-con