We use resonant soft x-ray scattering to study electronic reconstruction at the interface between the Mott insulator LaMnO3 and the "band" insulator SrMnO3. Superlattices of these two insulators were shown previously to have both ferromagnetism and metallic tendencies [Koida et al., Phys. Rev. B 66, 144418 (2002)]. By studying a judiciously chosen superlattice reflection we show that the interface density of states exhibits a pronounced peak at the Fermi level, similar to that predicted by Okamoto et al. [Phys. Rev. B 70, 241104(R) (2004)]. The intensity of this peak correlates with the conductivity and magnetization, suggesting it is the driver of metallic behavior. Our study demonstrates a general strategy for using RSXS to probe the electronic properties of heterostructure interfaces.
We report on the fabrication of all perovskite Mott insulator/band insulator YTiO3/CaTiO3 superlattices by pulsed laser deposition. The combination of in situ reflection high energy electron diffraction, X-ray diffraction, and X-ray reflectivity confirms the high quality of the films grown in a layer-by-layer mode. Electrical transport measurements reveal that a non-SrTiO3 based two dimensional electron gas system has formed at the YTiO3/CaTiO3 interface. These studies offer another route in the pursuit of complex oxide two-dimensional electron gas systems, which allows to obtain greater insig…
We investigate the electronic reconstruction at the interface between ferromagnetic metallic (FM) and antiferromagnetic insulating (AFI) manganites in superlattices using a two-orbital double-exchange model including superexchange interactions, Jahn-Teller lattice distortions, and long range Coulomb interactions. The magnetic and the transport properties critically depend on the thickness of the AFI layers. We focus on superlattices where the constituent parent manganites have the same electron density n = 0.6. The induced ferromagnetic moment in the AFI layers decreases monotonically with inc…
Here we report about the interface reconstruction in the recently discovered superconducting artificial superlattices based on insulating CaCuO2 and SrTiO3 blocks. Hard x-ray photoelectron spectroscopy shows that the valence bands alignment prevents any electronic reconstruction by direct charge transfer between the two blocks. We demonstrate that the electrostatic built-in potential is suppressed by oxygen redistribution in the alkaline earth interface planes. By using highly oxidizing growth conditions, the oxygen coordination in the reconstructed interfaces may be increased, resulting in th…
We explore manganite interface magnetism in epitaxially grown La0.7Sr0.3MnO3(LSMO)/SrTiO3 ultrathin superlattices (SL) along (110) orientation. we show that robust ferromagnetism persists down to four monolayers LSMO(MLs) (~1.1 nm in thickness), of which 50% Mn is at the interface state. Above eight MLs, the magnetic moment is nearly saturated to the theoretical value of 3.7u_B, with an estimated interface moment of 3.2u_B. In comparison to (100)-oriented SLs which were previously shown to have a spin canted ground state, (110)-oriented SLs exhibit stronger low-dimensional ferromagnetism and b…
Polarized neutron reflectivity measurements of a ferromagnetic [(LaMnO$_3$)$_{11.8}$/(SrMnO$_3$)$_{4.4}$]$_6$ superlattice reveal a modulated magnetic structure with an enhanced magnetization at the interfaces where LaMnO$_3$ was deposited on SrMnO$_3$ (LMO/SMO). However, the opposite interfaces (SMO/LMO) are found to have a reduced ferromagnetic moment. The magnetic asymmetry arises from the difference in lateral structural roughness of the two interfaces observed via electron microscopy, with strong ferromagnetism present at the interfaces that are atomically smooth over tens of nanometers. …
We have observed the pinned/biased moments in the superlattices consisting of ferromagnetic (FM) SrRuO3 (SRO) and antiferromagnetic (AFM) SrMnO3 (SMO)bilayer. The alternate stacking of SRO and SMO leading to a low field positive magnetoresistance with enhanced hysteretic field dependent magnetoresistance under the application of the out-of-plane magnetic field. We attribute these effects to the observed biased/pinned magnetic moments in the SRO layer in the vicinity of the interfaces. In addition, the biased/pinned moments can be oriented under the application of either the out-of-plane magnet…
We have measured photoemission spectra of SrTiO3/LaTiO3 superlattices with a topmost SrTiO3 layer of variable thickness. Finite coherent spectral weight with a clear Fermi cut-off was observed at chemically abrupt SrTiO3/LaTiO3 interfaces, indicating that an ``electronic reconstruction'' occurs at the interface between the Mott insulator LaTiO3 and the band insulator SrTiO3. For SrTiO3/LaTiO3 interfaces annealed at high temperatures (~ 1000 C), which leads to Sr/La atomic interdiffusion and hence to the formation of La1-xSrxTiO3-like material, the intensity of the incoherent part was found to …
We have investigated the magnetic properties of transition metal oxide superlattices with broken inversion symmetry composed of three different antiferromagnetic insulators, [NdMnO3/SrMnO3/LaMnO3]. In the superlattices studied here, we identify the emergence of a relaxor, glassy-like behavior below spin glass temperature, T=36K. Our results offer the possibility to study and utilize magnetically metastable devices confined in nano-scale interfaces.
The experimental observation that vanadate superlattices (LaVO$_3$)$_m$/SrVO$_3$ show ferromagnetism up to room temperature [U.\ Lüders {\it et al.}, Phys.\ Rev.\ B {\bf 80}, 241102R (2009)] is investigated by means of density functional theory. First, the influence of the density functional on the electronic and magnetic structure of bulk ${\rm LaVO_3}$ is discussed. Second, the band structure of a (LaVO$_3$)$_m$/SrVO$_3$ slab for $m=5$ and 6 is calculated. Very different behaviors for odd and even values of $m$ are found: In the odd case lattice relaxation results into a buckling of the inte…
We have performed ab initio calculations within the LDA+U method in the multilayered system (LaMnO$_3$)$_{2n}$ / (SrMnO$_3$)$_n$. Our results suggest a charge-ordered state that alternates Mn$^{3+}$ and Mn$^{4+}$ cations in a checkerboard in-plane pattern is developed at the interfacial layer, leading to a gap opening. Such an interfacial charge-ordered situation would be the energetically favored reconstruction between LaMnO$_3$ and SrMnO$_3$. This helps understanding the insulating behavior observed experimentally in these multilayers at intermediate values of $n$, whose origin is known to b…
The epitaxial stabilization of a single layer or superlattice structures composed of complex oxide materials on polar (111) surfaces is severely burdened by reconstructions at the interface, that commonly arise to neutralize the polarity. We report on the synthesis of high quality LaNiO$_3$/mLaAlO$_3$ pseudo cubic (111) superlattices on polar (111)-oriented LaAlO$_3$, the proposed complex oxide candidate for a topological insulating behavior. Comprehensive X-Ray diffraction measurements, RHEED, and element specific resonant X-ray absorption spectroscopy affirm their high structural and chemica…
Large magnetoelectric response in thin films is highly desired for high-throughput and high-density microelectronic applications. However, the d0 rule in single-phase compounds usually results in a weak interaction between ferroelectric and magnetic orders; the magnetoelectric coupling via elastic resonance in composites restricts their thin-film integration in broadband. Here, we effectuate a concurrence of ferroelectric-like and antiferromagnetic phase transitions in Sr2IrO4/SrTiO3 superlattices by artificial design periodically non-equivalent interfaces, where a maximum magnetoelectric coef…
Controlling the electronic properties of interfaces has enormous scientific and technological implications and has been recently extended from semiconductors to complex oxides which host emergent ground states not present in the parent materials. These oxide interfaces present a fundamentally new opportunity where, instead of conventional bandgap engineering, the electronic and magnetic properties can be optimized by engineering quantum many-body interactions. We utilize an integrated oxide molecular-beam epitaxy and angle-resolved photoemission spectroscopy system to synthesize and investigat…
We use a two-orbital double-exchange model including Jahn-Teller lattice distortions, superexchange interactions, and long-range Coulomb (LRC) interactions to investigate the origin of magnetically disordered interfaces between ferromagnetic metallic (FM) and antiferromagnetic insulating (AFI) manganites in FM/AFI superlattices. The induced magnetic moment in the AFI layer varies non-monotonically with increasing AFI layer width as seen in the experiment. We provide a framework for understanding this non-monotonic behavior which has a one-to-one correspondence with the magnetization of the FM …
The structure and interface characteristics of (LaVO3)6m(SrVO3)m superlattices deposited on (100)-SrTiO3 (STO) substrate were studied using Transmission Electron Microscopy (TEM). Cross-section TEM studies revealed that both LaVO3 (LVO) and SrVO3 (SVO) layers are good single crystal quality and epitaxially grown with respect to the substrate. It is evidenced that LVO layers are made of two orientational variants of a distorted perovskite compatible with bulk LaVO3 while SVO layers suffers from a tetragonal distortion due to the substrate induced stain. Electron Energy Loss Spectroscopy (EELS) …
Resonant soft x-ray absorption measurements at the O K edge on a SrMnO3/LaMnO3 superlattice show a shoulder at the energy of doped holes, which corresponds to the main peak of resonant scattering from the modulation in the doped hole density. Scattering line shape at the Mn L3,2 edges has a strong variation below the ferromagnetic transition temperature. This variation has a period equal to half the superlattice superperiod and follows the development of the ferromagnetic moment, pointing to a ferromagnetic phase developing at the interfaces. It occurs at the resonant energies for Mn3+ and Mn4…
Charge transfer and competing symmetry breaking drive orbital reconstruction and emergent ferromagnetism in insulating oxide superlattices
Indian Institute of Science（印度科学学院）；Deutsches Elektronen-Synchrotron DESY（德国电子同步加速器中心）；ALBA Synchrotron Light Source（阿尔巴同步辐射光源）；Advanced Photon Source, Argonne National Laboratory（阿贡国家实验室先进光子源）
The electronic symmetry of the SrTiO3/LaAlO3 interface was investigated by optical second harmonic generation, using superlattices with varying periodicity to study the evolution of the electronic reconstruction while avoiding substrate contributions. The superlattices show large perpendicular optical nonlinearity, which abruptly increases when the sublattice thickness goes above 3 unit cells, revealing substantial effects of the polar-nonpolar interface. The nonlinear 'active' area is primarily in SrTiO3, develops with increasing thickness, and extends up to 8 unit cells from the interface.
The recently discovered structural reconstruction in the cuprate superlattice (SrCuO$_2$)$_n$/(SrTiO$_3$)$_2$ has been investigated across the critical value of $n=5$ using resonant inelastic x-ray scattering (RIXS). We find that at the critical value of $n$, the cuprate layer remains largely in the bulk-like two-dimensional structure with a minority of Cu plaquettes being reconstructed. The partial reconstruction leads to quenching of the magnons starting at the $Γ$-point due to the minority plaquettes acting as scattering points. Although comparable in relative abundance, the doped charge im…
We have investigated the magnetic response of La0.7Sr0.3MnO3/SrRuO3 superlattices to biaxial in-plane strain applied in-situ. Superlattices grown on piezoelectric substrates of 0.72PbMg1/3Nb2/3O3-0.28PbTiO3(001) (PMN-PT) show strong antiferromagnetic coupling of the two ferromagnetic components. The coupling field of mu0HAF = 2.8 T is found to decrease by deltaHAF/delta epsilon ~ -520 mT %-1 under reversible biaxial strain mu0HAF at 80 K in a [La0.7Sr0.3MnO3(22)/SrRuO3(55)]15 superlattice. This reveals a significant strain effect on interfacial coupling. The applied in-plane compression enhanc…
We report a modulation of the in-plane magnetotransport in artificial manganite superlattice (SL) [(NdMnO3)n /(SrMnO3)n /(LaMnO3)n]m by varying the layer thickness n while keeping the total thickness of the structure constant. Charge transport in these heterostructures is confined to the interfaces and occurs via variable range hopping (VRH). Upon increasing n, the interfacial separation rises, leading to a suppression of the electrostatic screening between carriers of neighboring interfaces and the opening of a Coulomb gap at the Fermi level (EF). The high-field magnetoresistance (MR) is univ…
The electronic structure of interfaces between YBa$_2$Cu$_3$O$_6$ and SrTiO$_3$ is studied using local spin density approximation (LSDA) with intra-atomic Coulomb repulsion (LSDA+U). We find a metallic state in cuprate/titanate heterostructures with the hole carriers concentrated substantially in the CuO$_2$-layers and in the first interface TiO$_2$ and SrO planes. This effective interface doping appears due to the polarity of interfaces, caused by the first incomplete copper oxide unit cell. Interface-induced high pre-doping of CuO$_2$-layers is a key mechanism controlling the superconducting…
We report a highly unusual angular variation of the upper critical field (H_c2) in epitaxial superlattices CeCoIn_5(n)/YbCoIn_5(5), formed by alternating layers of n and a 5 unit-cell thick heavy-fermion superconductor CeCoIn_5 with a strong Pauli effect and normal metal YbCoIn_5, respectively. For the n=3 superlattice, H_{c2}(θ) changes smoothly as a function of the field angle θ. However, close to the superconducting transition temperature, H_{c2}(θ) exhibits a cusp near the parallel field (θ=0 deg). This cusp behavior disappears for n=4 and 5 superlattices. This sudden disappearance suggest…
Ultra-thin tri-color (tri-layer) titanate superlattices ([3u.c. LaTiO3/2u.c. SrTiO3/3u.c. YTiO3], u.c. = unit cells) were grown in a layer-by-layer way on single crystal TbScO3 (110) substrates by pulsed laser deposition. High sample quality and electronic structure were characterized by the combination of in-situ photoelectron and ex-situ structure and surface morphology probes. Temperature-dependent sheet resistance indicates the presence of metallic interfaces in both [3u.c. LaTiO3/2u.c. SrTiO3] bi-layers and all the tri-color structures, whereas a [3u.c. YTiO3/2u.c. SrTiO3] bi-layer shows …
The exchange coupling at the interfaces of magnetic superlattices consisting of ferromagnetic $SrRuO_3$ and antiferromagnetic $SrMnO_3$ grown on (001) oriented $SrTiO_3$ is studied with in-plane and out-of-plane orientations, with respect to the substrate plane, of the cooling magnetic field. The magnetization of the in-plane, field cooled hysteresis loop is lower than the corresponding in-plane zero-field-cooled hysteresis loop. The out-of-plane field cooled hysteresis loop is shifted, from the origin, along the graphical magnetization axis. We attribute this irreversible rotation of the mome…
We studied the magnetic properties of La$_{0.7}$Ca$_{0.3}$MnO$_3$ / YBa$_2$Cu$_3$O$_{7-δ}$ superlattices. Magnetometry showed that with increasing YBa$_2$Cu$_3$O$_{7-δ}$ layer thickness the saturation magnetization per La$_{0.7}$Ca$_{0.3}$MnO$_3$ layer decreases. From polarized neutron reflectometry we determined that this magnetization reduction is due to an inhomogenous magnetization depth profile arising from the suppression of magnetization near the La$_{0.7}$Ca$_{0.3}$MnO$_3$ / YBa$_2$Cu$_3$O$_{7-δ}$ interface. Electron energy loss spectroscopy indicates an increased 3d band occupation of…
The formation of a skyrmion crystal and its phase transition are studied taking into account the Dzyaloshinskii-Moriya (DM) interaction at the interface between a ferroelectric layer and a magnetic layer in a superlattice. The frustration is introduced in both magnetic and ferroelectric films. The films have the simple cubic lattice structure. Spins inside magnetic layers are Heisenberg spins interacting with each other via nearest-neighbor (NN) exchange $J^m$ and next-nearest-neighbor (NNN) exchange $J^{2m}$. Polarizations in the ferroelectric layers are assumed to be of Ising type with NN an…
We show, by means of low-energy muon spin rotation measurements, that few-unit-cells thick La(2)CuO(4) layers synthesized digitally by molecular beam epitaxy synthesis are antiferromagnetically ordered. Below a thickness of about 5 CuO(2) layers the long-range ordered state breaks down, and a magnetic state appears with enhanced quantum fluctuations and a reduced spin stiffness. This magnetic state can exist in close proximity (few Angstrom) to high-temperature superconducting layers, without transmitting supercurrents.
The crystalline structure, anisotropic magnetoresistance (AMR), and magnetization of La0.7Sr0.3MnO3/SrTiO3 (LSMO/STO) superlattices grown by an rf sputtering system are systematically analyzed to study the spin polarization of manganite at interfaces. A perfectly epitaxial growth with sharp interfaces between LSMO and STO layers is confirmed by the transmission electron microscopy (TEM) image and the x-ray diffraction. The presence of positive low-temperature AMR in LSMO/STO superlattices with thinner LSMO layers or thicker STO layers implies that two bands of majority and minority character c…
We use resonant soft x-ray scattering (RSXS) to quantify the hole distribution in a superlattice of insulating La2CuO4 (LCO) and overdoped La_{2-x}Sr_{x}CuO4 (LSCO). Despite its non-superconducting constituents, this structure is superconducting with T_{c}=38 K. We found that the conducting holes redistribute electronically from LSCO to the LCO layers. The LCO layers were found to be optimally doped, suggesting they are the main drivers of superconductivity. Our results demonstrate the utility of RSXS for separating electronic from structural effects at oxide interfaces.
X-ray absorption spectroscopy and resonant soft x-ray reflectivity show a non-uniform distribution of oxygen holes in a La2NiO4 - La2CuO4 (LNO-LCO) superlattice, with excess holes concentrated in the LNO layers. Weak ferromagnetism with Tc = 160 K suggests a coordinated tilting of NiO6 octahedra, similar to that of bulk LNO. Ni d3z2-r2 orbitals within the LNO layers have a spatially variable occupation. This variation of the Ni valence near LNO-LCO interfaces is observed with resonant soft x-ray reflectivity at the Ni L edge, at a reflection suppressed by the symmetry of the structure, and is …
Perovskite nickelate heterostructure consisting of single unit cell of EuNiO$_3$ and LaNiO$_3$ have been grown on a set of single crystalline substrates by pulsed laser interval deposition to investigate the effect of epitaxial strain on electronic and magnetic properties at the extreme interface limit. Despite the variation of substrate in-plane lattice constants and lattice symmetry, the structural response to heterostructuring is primarily controlled by the presence of EuNiO$_3$ layer. In sharp contrast to bulk LaNiO$_3$ or EuNiO$_3$, the superlattices grown under tensile strains exhibit me…
Unconventional superconductivity and magnetism are intertwined on a microscopic level in a wide class of materials, including high-$T_c$ cuprates, iron pnictides, and heavy-fermion compounds. A new approach to this most fundamental and hotly debated subject focuses on the role of interactions between superconducting electrons and bosonic fluctuations at the interface between adjacent layers in heterostructures. A recent state-of-the-art molecular-beam-epitaxy technique has enabled us to fabricate superlattices consisting of different heavy-fermion compounds with atomic thickness. These Kondo s…
Interface magnetic coupling and magnetization dynamic of La$_{2/3}$Sr$_{1/3}$MnO$_3$ single layer and (La$_{2/3}$Sr$_{1/3}$MnO$_3$/SrRuO$_3$)$_n$ (n = 1, 5) superlattice on SrTiO$_3$(001) substrate
We report on the electronic properties of superlattices composed of three different antiferromagnetic insulators, NdMnO3/SrMnO3/LaMnO3 grown on SrTiO3 substrates. Photoemission spectra obtained by tuning the x-ray energy at the Mn 2p -> 3d edge show a Fermi cut-off, indicating metallic behavior mainly originating from Mn e_g electrons. Furthermore, the density of states near the Fermi energy and the magnetization obey a similar temperature dependence, suggesting a correlation between the spin and charge degrees of freedom at the interfaces of these oxides.
A combination of spectroscopic probes was used to develop a detailed experimental description of the transport and magnetic properties of superlattices composed of the paramagnetic metal CaRuO$_3$ and the antiferromagnetic insulator CaMnO$_3$. The charge carrier density and Ru valence state in the superlattices are not significantly different from those of bulk CaRuO$_3$. The small charge transfer across the interface implied by these observations confirms predictions derived from density functional calculations. However, a ferromagnetic polarization due to canted Mn spins penetrates 3-4 unit …
Here we present polarized neutron reflectometry measurements exploring thin film heterostructures comprised of a strongly correlated Mott state, GdTiO$_3$, embedded with SrTiO$_3$ quantum wells. Our results reveal that the net ferromagnetism inherent to the Mott GdTiO$_3$ matrix propagates into the nominally nonmagnetic SrTiO$_3$ quantum wells and tracks the magnetic order parameter of the host Mott insulating matrix. Beyond a well thickness of 5 SrO layers, the magnetic moment within the wells is dramatically suppressed, suggesting that quenched well magnetism comprises the likely origin of q…
We investigated the magnetic and optical properties of [(LaMnO3)n/(SrTiO3)8]20 (n = 1, 2, and 8) superlattices grown by pulsed laser deposition. We found a weak ferromagnetic and semiconducting state developed in all superlattices. An analysis of the optical conductivity showed that the LaMnO3 layers in the superlattices were slightly doped. The amount of doping was almost identical regardless of the LaMnO3 layer thickness up to eight unit cells, suggesting that the effect is not limited to the interface. On the other hand, the magnetic ordering became less stable as the LaMnO3 layer thickness…
An interface modification of LCMO-BTO superlattices was found to massively influence magnetic and magnetotransport properties. Moreover it determines the crystal structure of the manganite layers, changing it from orthorhombic (Pnma) for the conventional superlattice (cSL), to rhombohedral (R-3c) for the modified one (mSL). While the cSL shows extremely nonlinear ac transport, the mSL is an electrically homogeneous material. The observations go beyond an oversimplified picture of dead interface layers and evidence the importance of electronic correlations at perovskite interfaces.
The paradigm of electrons interacting with a periodic lattice potential is central to solid-state physics. Semiconductor heterostructures and ultracold neutral atomic lattices capture many of the essential properties of 1D electronic systems. However, fully one-dimensional superlattices are highly challenging to fabricate in the solid state due to the inherently small length scales involved. Conductive atomic-force microscope (c-AFM) lithography has recently been demonstrated to create ballistic few-mode electron waveguides with highly quantized conductance and strongly attractive electron-ele…
We used infrared spectroscopic ellipsometry to investigate the electronic properties of LaTiO3/SrTiO3 superlattices (SLs). Our results indicated that, independent of the SL periodicity and individual layer-thickness, the SLs exhibited a Drude metallic response with sheet carrier density per interface ~3x10^14 cm^-2. This is probably due to the leakage of d-electrons at interfaces from the Mott insulator LaTiO3 to the band insulator SrTiO3. We observed a carrier relaxation time ~ 35 fs and mobility ~ 35 cm^2V^-1s^-1 at 10 K, and an unusual temperature dependence of carrier density that was attr…
The magnetic and electronic modifications induced at the interfaces in (SrMnO$_{3}$)$_{n}$/(LaMnO$_{3}$)$_{2n}$ superlattices have been investigated by linear and circular magnetic dichroism in the Mn L$_{2,3}$ x-ray absorption spectra. Together with theoretical calculations, our data demonstrate that the charge redistribution across interfaces favors in-plane ferromagnetic (FM) order and $e_{g}(x^{2}-y^{2})$ orbital occupation, in agreement with the average strain. Far from interfaces, inside LaMnO$_3$, electron localization and local strain favor antiferromagnetism (AFM) and $e_{g}(3z^{2}-r^…
LaNiO$_3$ (LNO) is an intriguing member of the rare-earth nickelates in exhibiting a metal-insulator transition for a critical film thickness of about 4 unit cells [Son et al., Appl. Phys. Lett. 96, 062114 (2010)]; however, such thin films also show a transition to a metallic state in superlattices with SrTiO$_3$ (STO) [Son et al., Appl. Phys. Lett. 97, 202109 (2010)]. In order to better understand this transition, we have studied a strained LNO/STO superlattice with 10 repeats of [4 unit-cell LNO/3 unit-cell STO] grown on an (LaAlO$_3$)$_{0.3}$(Sr$_2$AlTaO$_6$)$_{0.7}$ substrate using soft x-…
Heterostructures of mixed-valence manganites are still under intense scrutiny, due to the occurrence of exotic quantum phenomena linked to electronic correlation and interfacial composition. For instance, if two anti-ferromagnetic insulators as LaMnO$_3$ and SrMnO$_3$ are grown in a (001)-oriented superlattice, a half-metallic ferromagnet may form, provided that the thickness is sufficiently small to allow tunneling across interfaces. In this article, we employ electronic structure calculations to show that all the layers of a (111)-oriented LaMnO$_3$|SrMnO$_3$ superlattice retain a half-metal…
Perpendicular magnetic anisotropy (PMA) plays a critical role in the development of spintronics, thereby demanding new strategies to control PMA. Here we demonstrate a conceptually new type of interface induced PMA that is controlled by oxygen octahedral rotation. In superlattices comprised of La$_{1-x}$Sr$_{x}$MnO$_{3}$ and SrIrO$_{3}$, we find that all superlattices (0$\leq$x$\leq$1) exhibit ferromagnetism despite the fact that La$_{1-x}$Sr$_{x}$MnO$_{3}$ is antiferromagnetic for x$>$0.5. PMA as high as 4$\times$10$^6$ erg/cm$^3$ is observed by increasing x and attributed to a decrease of ox…
The effects of reduced dimensions and the interfaces on antiferromagnetic quantum criticality are studied in epitaxial Kondo superlattices, with alternating $n$ layers of heavy-fermion antiferromagnet CeRhIn$_5$ and 7 layers of normal metal YbRhIn$_5$. As $n$ is reduced, the Kondo coherence temperature is suppressed due to the reduction of effective Kondo screening. The Néel temperature is gradually suppressed as $n$ decreases and the quasiparticle mass is strongly enhanced, implying dimensional control toward quantum criticality. Magnetotransport measurements reveal that a quantum critical po…
Charge transfer in oxide heterostructures can be tuned to promote emergent interfacial states, and accordingly, has been the subject of intense study in recent years. However, accessing the physics at these interfaces, which are often buried deep below the sample surface, remains difficult. Addressing this challenge requires techniques capable of measuring the local electronic structure with high-resolution depth dependence. Here, we have used linearly-polarized resonant X-ray reflectometry (RXR) as a means to visualize charge transfer in oxide superlattices with atomic layer precision. From o…
Interface can be a fertile ground for exotic quantum states, including topological superconductivity, Majorana mode, fractal quantum Hall effect, unconventional superconductivity, Mott insulator, etc. Here we grow single-unit-cell (1UC) FeTe film on NbSe2 single crystal by molecular beam epitaxy (MBE) and investigate the film in-situ with home-made cryogenic scanning tunneling microscopy (STM) and non-contact atomic force microscopy (AFM) combined system. We find different stripe-like superlattice modulations on grown FeTe film with different misorientation angles with respect to NbSe2 substra…