Perovskite-type cobalt oxide at the multiferroic Co/Pb Zr$_{0.2}$Ti$_{0.8}$O$_{3}$ interface
K. Mohseni, A. Polyakov, H. B. Vasili, I. V. Maznichenko, S. Ostanin, A. Quindeau, N. Jedrecy, E. Fonda, L. V. Bekenov, V. N. Antonov, P. Gargani, M. Valvidares… 展开作者
K. Mohseni, A. Polyakov, H. B. Vasili, I. V. Maznichenko, S. Ostanin, A. Quindeau, N. Jedrecy, E. Fonda, L. V. Bekenov, V. N. Antonov, P. Gargani, M. Valvidares, I. Mertig, S. S. P. Parkin, A. Ernst, H. L. Meyerheim
Magnetic Tunnel Junctions whose basic element consists of two ferromagnetic electrodes separated by an insulating non-magnetic barrier have become intensely studied and used in non-volatile spintronic devices. Since ballistic tunnel of spin-polarized electrons sensitively depends on the chemical composition and the atomic geometry of the lead/barrier interfaces their proper design is a key issue for achieving the required functionality of the devices such as e.g. a high tunnel magneto resistance. An important leap in the development of novel spintronic devices is to replace the insulating barrier by a ferroelectric which adds new additional functionality induced by the polarization direction in the barrier giving rise to the tunnel electro resistance (TER). The multiferroic tunnel junction Co/PbZr$_{0.2}$Ti$_{0.8}$O$_{3}$/La$_{2/3}$Sr$_{1/3}$MnO$_3$ (Co/PZT/LSMO) represents an archetype system for which - despite intense studies - no consensus exists for the interface geometry and their effect on transport properties. Here we provide the first analysis of the Co/PZT interface at the atomic scale using complementary techniques, namely x-ray diffraction and extended x-ray absorption fine structure in combination with x-ray magnetic circular dichroism and ab-initio calculations. The Co/PZT interface consists of one perovskite-type cobalt oxide unit cell [CoO$_{2}$/CoO/Ti(Zr)O$_{2}$] on which a locally ordered cobalt film grows. Magnetic moments (m) of cobalt lie in the range between m=2.3 and m=2.7$μ_{B}$, while for the interfacial titanium atoms they are small (m=+0.005 $μ_{B}$) and parallel to cobalt which is attributed to the presence of the cobalt-oxide interface layers. These insights into the atomistic relation between interface and magnetic properties is expected to pave the way for future high TER devices.
This review devoted to multiferroic properties of Bismuth-based perovskites falls into two parts. The first part focuses on BiFeO3 and summarizes the recent progress made in the studies of its pressure-temperature phase diagram and magnetoelectric coupling phenomena. The second part discusses in a more general way the issue of polar - and multiferroic - phases in BiBO3 perovskites and the competition between ferroelectricity and other structural instabilities, from an inventory of recently synthetized compounds.
The possibility to segregate cobalt and iron in a single perovskite, at a nanoscale in the form of layers has been investigated, using sol gel technic synthesis. Quite remarkably, it is shown that such a nanoscale ordering, which can only be detected by a combined HAADF-STEM and EELS study, has a significant impact upon the magnetic properties of this SmFe0.5Co0.5O3 oxide. This suggests that careful nanoscale characterization of oxides will be necessary in the future before proceeding to a viable interpretation of their physical properties, at least in the field of magnetism.
Rare earth perovskite cobaltites are increasingly recognized as materials of importance due to rich physics and chemistry in their ordered-disordered structure for the same composition. Apart from colossal magnetoresistance effect, like manganites, the different forms of cobaltites exhibit interesting phenomena including spin, charge and orbital ordering, electronic phase separation, insulator-metal transition, large thermoelectric power at low temperature. Moreover, the cobaltites which display colossal magnetoresistance effect could be used as read heads in magnetic data storage and also in …
We have used a shell model to study the phonon dynamics of multiferroic manganites RMnO3 (R= Tb, Dy, Ho). The calculated phonon dynamical properties, crystal structure, Raman frequencies and specific heat are found to be in good agreement with the available experimental data. Besides, the phonon density of states, elastic constants and phonon dispersion curves along high symmetry directions (sigma, delta and lambda) have also been computed. A zone-center imaginary Au mode is revealed in these phonon dispersion curves, which indicates the occurrence of metastability of the perovskite phase. The…
We propose experimental verification and theoretical explanation of magnetic anomalies in the complex Fe-contained double perovskite multiferroics like PbFe$_{1/2}$Nb$_{1/2}$O$_3$. The theoretical part is based on our model of coexistence of long-range magnetic order and spin glass in the above substances. In our model, the exchange interaction is anisotropic, coupling antiferromagnetically $z$ spin components of Fe$^{3+}$ ions. At the same time, the $xy$ components are coupled by much weaker exchange interaction of ferromagnetic sign. In the system with spatial disorder (half of corresponding…
Many multiferroic materials, with various chemical compositions and crystal structures, have been discovered in the past years. Among these multiferroics, some perovskite manganites with ferroelectricity driven by magnetic orders are of particular interest. In these multiferroic perovskite manganites, not only their multiferroic properties are quite prominent, but also the involved physical mechanisms are very plenty and representative. In this Brief Review, we will introduce some recent theoretical and experimental progress on multiferroic manganites.
In this study we have compared magnetic, magnetostrictive and piezomagnetic properties of isotropic and anisotropic cobalt ferrite pellets. The isotropic sample was prepared by the ceramic method while the sample exhibiting uniaxial anisotropy was made by reactive sintering using Spark Plasma Sintering (SPS). This technique permits to induce a magnetic anisotropy in cobalt ferrite in the direction of the applied pressure during SPS process. Sample with uniaxial anisotropy revealed a higher longitudinal magnetostriction and piezomagnetism compared to the isotropic sample, but the transversal ma…
Despite the great technological and scientific importance, a well-controlled coupled behavior in magnetoelectric multiferroic materials at room temperature remains challenging. We demonstrate that the self-ordered A2BBO6 (e.g., A = La, B = Mn, and B = Ni) double perovskites provide a unique alternative opportunity to control and/or to induce such behavior in oxides. In this paper, we outline and discuss the various challenges and bottleneck issues related to this class of materials using La2NiMnO6 as a prototype. Details of the synthesis strategies, using pulsed laser deposition as a central t…
In this paper we investigated the influence of the rare-earth ionic radii on the spin-phonon coupling in RE2NiMnO6 double perovskites by Raman spectroscopy. Spin-phonon in dense Nd2NiMnO6 and Gd2NiMnO6 ceramics were investigated by Raman spectroscopy at low temperatures. The magnitude of the coupling observed in comparison with other isostructural compounds shows that it is not influenced by the rare-earth ionic radius, as well as the deviation of the position of the stretching phonon in the ferromagnetic phase with relation to the anharmonic contributions follows a power law.
Double perovskites provide a unique opportunity to induce and control multiferroic behaviors in oxide systems. The appealing possibility to design materials with a strong coupling between the magnetization and the polarization fields may be achieved in this family since these magnetic insulators can present structural self-ordering in the appropriate growth conditions. We have studied the functional properties of La2CoMnO6 and Bi2CoMnO6 epitaxial thin films grown by pulsed laser deposition. Cation-ordered La2CoMnO6 films display a magnetic Curie temperature of 250 K while cation-disordered Bi2…
We investigate a magnetic hysteresis loop with a remanent moment that couples to electric polarization to create coupled hysteretic multiferroic behavior in Lu2MnCoO6. Measurements of elastic neutron diffraction, muon spin relaxation, and micro-Hall magnetometry demonstrate an unusual mechanism for the magnetic hysteresis, namely the hysteretic evolution of a microscopic magnetic order, and not classic ferromagnetic domain effects. We show how the frustrated spin system evolves from antiferromagnetism with an incommensurate long-wavelength modulation and strong fluctuations towards a net magne…
In this article, we perform the symmetry analysis of perovskite-based multiferroics: bismuth ferrite (BiFeO3)-like, orthochromites (RCrO3), and Ruddlesden-Popper perovskites (Ca3Mn2O7-like), being the typical representatives of multiferroics of the trigonal, rhombic, and tetragonal crystal families and explore the effect of crystallographic distortions on magnetoelectric properties. We determine the principal order parameters for each of the considered structures and obtain their invariant combinations consistent with the particular symmetry. This approach allowed us to analyze the features of…
We investigate the electronic, ferroelectric and magnetic properties of KTaO3/PbTiO3 interfaces by using conventional density functional theory (DFT) and advanced DFT such as hybrid functional HSE06. We show that doped holes in valence bands or electrons in conduction bands give rise to ferromagnetism at the interfaces. The ferromagnetic states are ground states for both hole-doped (p-type) and electron-doped (n-type) interfaces by comparison with their corresponding nonmagnetic and antiferromagnetic states. Carriers (holes or electrons) concentrate near the interface to screen the polarizatio…
Structural, impedance, ferroelectric and magnetic properties were examined in multiferroic Bi_{2}Fe_{4(1-x)}Co_{4x}O_{9} (0$\leq$x$\leq$0.02) ceramics synthesized via solid-state reaction method. X-ray diffraction analysis and Rietveld refinement showed secondary phase formation (for x$\geq$0.01) which was subsequently confirmed from room temperature Raman spectroscopy study. The frequency dependence of impedance and electric modulus of the material showed the presence of non-Debye type relaxation in all the samples. The values of the activation energies calculated from imaginary impedance and…
With the perovskite multiferroic RMnO3 (R = Gd, Tb, Dy) as guidance, we argue that the Dzyaloshinskii-Moriya interaction (DMI) provides the microscopic mechanism for the coexistence and strong coupling between ferroelectricity and incommensurate magnetism. We use Monte-Carlo simulations and zero temperature exact calculations to study a model incorporating the double-exchange, superexchange, Jahn-Teller and DMI terms. The phase diagram contains a multiferroic phase between A and E antiferromagnetic phases, in excellent agreement with experiments.
We investigate the crystal structure in multiferroic tetragonal perovskite Sr$_{1/2}$Ba$_{1/2}$MnO$_3$ with high accuracy of the order of 10$^{-3}$ Angstrom for an atomic displacement. The large atomic displacement for Mn ion from the centerosymmetric position, comparable with the off-centering distortion in the tetragonal ferroelectric BaTiO$_3$, is observed in the ferroelectric phase ($T_\mathrm{N}$ $\leq$ $T$ $\leq$ $T_\mathrm{C}$). In stark contrast, in the multiferroic phase ($T$ $\leq$ $T_\mathrm{N}$), the atomic displacement for Mn ion is suppressed, but those for O ions are enlarged. T…
Antiferromagnetic Bi_{2}Fe_{4}O_{9} (BFO), lightly substituted by cobalt is studied for magnetodielectricity. The substitution causes a substantial decrease in the Neel temperature (T_N) from 250 K (in parent sample, BFO) to 152 K (in 2% Co substituted sample). At the same time, the substituted samples display a pronounced irreversibility in the ZFC-FC magnetization data for T $<$ 370 K and opening of hysteresis in the M-H plot, thus signifying the onset of weak ferromagnetism (FM) and magnetic glassiness. The induced magnetic glassiness is found to slow down the dynamics such that the magneti…
In this article the mechanism of the linear magnetoelectric (ME) effect in the rhombohedral multiferroic BiFeO$_3$ is considered. The study is based on the symmetry approach of the GinzburgLandau type, in which polarization, antiferrodistortion, and antiferromagnetic momentum vectors are viewed as ordering parameters. We demonstrate that the linear ME effect in BFO is caused by reorientation of the antiferrodistortion vector in either electric or magnetic field. The numerical estimations, which show quantitative agreement with the results of the recent measurements in film samples, have been p…
We present a new member of the multiferroic oxides, Lu$_2$MnCoO$_6$, which we have investigated using X-ray diffraction, neutron diffraction, specific heat, magnetization, electric polarization, and dielectric constant measurements. This material possesses an electric polarization strongly coupled to a net magnetization below 35 K, despite the antiferromagnetic ordering of the $S = 3/2$ Mn$^{4+}$ and Co$^{2+}$ spins in an $\uparrow \uparrow \downarrow \downarrow$ configuration along the c-direction. We discuss the magnetic order in terms of a condensation of domain boundaries between $\uparrow…
The perovskite (1-x)YMnO$_3$-xBiFeO$_3$ binary system is very promising because of its multiferroic end members. Nanocrystalline phases have been recently obtained by mechanosynthesis across the system, and the perovskite structural evolution has been described. Two continuous solid solutions with orthorhombic Pnma and rhombohedral R3c symmetries were found, which coexist within a broad compositional interval of 0.5 < x < 0.9. This might be a polar-nonpolar morphotropic phase boundary region, at which strong phase-change magnetoelectric responses can be expected. A major issue is phase decompo…
In this work multiferroic thin films of Bi containing perovskite oxides are discussed, where the driving force for ferroelectricity are the Bi3+ lone-pair electrons. First, a brief introduction of Bi containing multiferroic perovskite oxides will be presented to describe the mechanisms for establishing magnetic and ferroelectric order in these compounds and some recent developments in this field of research are reported. The second section addresses experimental aspects of epitaxial thin film growth of BiMnO3, (Bi0.9La0.1)2NiMnO6 (BLNMO) and BiFeO3 thin films by pulsed laser deposition. The th…
The magnetic order, spin dynamics, and crystal structure of the multiferroic Sr0.56Ba0.44MnO3 have been investigated using neutron and x-ray scattering. Ferroelectricity develops at TC=305 K with a polarization of 4.2 microC/cm2 associated with the displacements of the Mn ions, while the Mn4+ spins order below TN = 200 K into a simple G-type commensurate magnetic structure. Below TN the ferroelectric order decreases dramatically demonstrating that the two order parameters are strongly coupled. The ground state spin dynamics are characterized by a spin gap of 4.6(5) meV and the magnon density o…
We use resonant and non-resonant X-ray diffraction measurements in combination with first-principles electronic structure calculations and Monte Carlo simulations to study the relationship between crystal structure and multiferroic orders in the orthorhombic perovskite manganites, o-$R$MnO$_3$ ($R$ is a rare-earth cation or Y). In particular, we focus on how the internal lattice parameters (Mn-O bond lengths and Mn-O-Mn bond angles) evolve under chemical pressure and epitaxial strain, and the effect of these structural variations on the microscopic exchange interactions and long-range magnetic…
Optimal materials to induce bulk photovoltaic effects should lack inversion symmetry and have an optical gap matching the energies of visible radiation. Ferroelectric perovskite oxides such as BaTiO$_3$ and PbTiO$_3$ exhibit substantial polarization and stability, but have the disadvantage of excessively large band gaps. We use both density functional theory and dynamical mean field theory calculations to design a new class of Mott multiferroics--double perovskite oxides $A_2$VFeO$_6$ ($A$=Ba, Pb, etc). While neither perovskite $A$VO$_3$ nor $A$FeO$_3$ is ferroelectric, in the double perovskit…
Rare earth based cobalt-ruthenium double perovskites A$_2$CoRuO$_6$ (A = La, Pr, Nd and Sm) were synthesized and investigated for their structural and magnetic properties. All the compounds crystallize in the monoclinic $P2_1/n$ structure with the indication of antisite disorder between Co and Ru sites. While, La compound is already reported to have an antiferromagnetic state below 27 K, the Pr, Nd and Sm systems are found to be ferrimagnetic below $T_c$ = 46, 55 and 78 K respectively. Field dependent magnetization data indicate prominent hysteresis loop below $T_c$ in the samples containing m…
Oxygen vacancies in transition metal oxides facilitate catalysis critical for energy storage and generation. However, it has proven elusive to promote vacancies at the lower temperatures required for operation in devices such as metal-air batteries and portable fuel cells. Here, we use thin films of the perovskite-based strontium cobaltite (SrCoOx) to show that epitaxial strain is a powerful tool towards manipulating the oxygen content under conditions consistent with the oxygen evolution reaction, yielding increasingly oxygen deficient states in an environment where the cobaltite would normal…
A new nanoscale ordered perovskite cobaltite, which consists of 90 degree ordered domains of the layered-112 LaBaCo2O6 has been evidenced by high resolution- transmission electron microscopy. This new form, like the disordered La0.5Ba0.5CoO3 and ordered LaBaCo2O6, exhibits a ferromagnetic transition at TC around 179 K. However, it differs from the two previous forms by its strong magnetic anisotropy, and correlatively by its high value of coercivity (0.42 Tesla) at low temperature. We suggest that this behaviour originates from the locking of magnetic spins in the 90 degree oriented nano-domai…
The theoretical description of the nanostructured Pb(Fe1/2Ta1/2)x(Zr1/2Ti1/2)1-xO3 (PFTx-PZT(1-x)) and Pb(Fe1/2Nb1/2)x(Zr1/2Ti1/2)1-xO3 (PFNx-PZT(1-x)) intriguing ferromagnetic, ferroelectric and magnetoelectric properties at temperatures higher than 100 K are absent to date. The goal of this work is to propose the theoretical description of the physical nature and the mechanisms of the aforementioned properties, including room temperature ferromagnetism, phase diagram dependence on the composition x with a special attention to the multiferroic properties at room temperature, including anomalo…
Multiferroics with coupling between ferroelectricity and magnetism have been pursued for decades. However, their magnetoelectric performances remain limited due to the common trade-off between ferroelectricity and magnetism. Here, a family of nitride perovskites is proposed as multiferroics with prominent physical properties and nontrivial mechanisms. Taking GdWN$_3$ as a prototype, our first-principles calculations found that its perovskite phases own large polarizations (e.g. $111.3$ $μ$C/cm$^2$ for the $R3c$ phase) and a magnetic moment $7$ $μ_{\rm B}$/Gd$^{3+}$. More interestingly, its fer…
We theoretically study origins of the ferroelectricity in the multiferroic phases of the rare-earth (R) Mn perovskites, RMnO3, by constructing a realistic spin model including the spin-phonon coupling, which reproduces the entire experimental phase diagram in the plane of temperature and Mn-O-Mn bond angle for the first time. Surprisingly we reveal a significant contribution of the symmetric (S.S)-type magnetostriction to the ferroelectricity even in a spin-spiral-based multiferroic phase, which can be larger than the usually expected antisymmetric (SxS)-type contribution. This explains well t…
Epitaxial strain has been shown to drive structural phase transitions along with novel functionalities in perovskite-based thin-films. Aliovalent doping at the A-site can drive an insulator-to-metal and magnetic transitions in perovskites along with a variety of interesting structural and electronic phenomena. Using first-principles calculations, we demonstrate here, how coupling epitaxial strain with A-site hole doping in a multiferroic double perovskite, Bi2FeCrO6, could lead to mitigation of issues related to anti-site defects and lowered magnetisation in thin-films of the material. We also…
The link between the crystal distortions of the perovskite structure and the magnetic exchange interaction, the single-ion anisotropy (SIA) and the Dzyaloshinsky-Moriya (DM) interaction are investigated by means of density-functional calculations. Using BiFeO$_3$ and LaFeO$_3$ as model systems, we quantify the relationship between the oxygen octahedra rotations, the ferroelectricity and the weak ferromagnetism (wFM). We recover the fact that the wFM is due to the DM interaction induced by the oxygen octahedra rotations. We find a simple relationship between the wFM, the oxygen rotation amplitu…
Magnetoelectric Coupling in Nickel-Cobalt Ferrite and Lanthanum Ferrite Heterostructure Composites: Experimental Evidence and Simulation-Driven Insights
Recently, the perovskite BiCoO$_3$ has been shown experimentally to be isostructural with PbTiO$_3$, while simultaneously the $d^6$ Co$^{3+}$ ion has a high spin ground state with $C$-type antiferromagnetic ordering. Using hybrid density functional calculations, we investigate the atomic, electronic and magnetic structure of BiCoO$_3$ to elucidate the origin of the multiferroic state. To begin with, we perform a qualitative trend sudy of the role of $d$ electrons in affecting the tendency for perovskite materials to exhibit a ferroelectric distortion; this work initially explores a qualitative…
We report the observation of unusual exchange bias phenomena in the doped perovskite cobaltites La_{1-x}Sr_{x}CoO_{3} (x = 0.15, 0.18, and 0.30) in which a spontaneous phase separation into ferromagnetic clusters embedded in a non-ferromagnetic matrix occurs. When the La_{1-x}Sr_{x}CoO_{3} samples are cooled in a static magnetic field through a freezing temperature, the magnetization hysteresis loops exhibit exchange bias, i.e., the loops shift to the negative field and the magnetization becomes asymmetric. Moreover, exchange bias disappears when the measuring magnetic field is high enough. Th…
A dielectric anomaly has been found near the incommensurate to commensurate antiferromagnetic phase transition (TN2=230 K) in YBaCuFeO5 ceramics, a compound which crystallizes in an ordered perovskite structure. The existence of electric polarization below TN2 suggests the magnetism induced charge polarization effect that is also confirmed by its strong magnetic field dependence below TN2. Accordingly, the peak near TN2 of the magnetodielectric effect indicates a maximum of magnetodielectric susceptibility near the spin reorientation transition. Considering the abundance of magnetic compounds …
Complete magnetoelectric (ME) phase diagrams of orthorhombic $R$MnO$_{3}$ with and without magnetic moments on the $R$ ions have been established. Three kinds of multiferroic ground states, the $ab$-cycloidal, the $bc$-cycloidal, and the collinear $E$-type phases, have been identified by the distinct ME responses. The electric polarization of the $E$-type phase dominated by the symmetric spin exchange ($bm{S}_{i} cdot bm{S}_{j}$) is more than 10 times as large as that of the $bc$-cycloidal phase dominated by the antisymmetric one ($bm{S}_{i} times bm{S}_{j}$), and the ME response is enhanced n…
We study theoretically the electromagnon and its optical spectrum (OS) of the terahertz-frequency regime in the magnetic-spiral-induced multiferroic phases of the rare-earth (R) Mn perovskites, RMnO3, taking into account the elliptical deformation or the higher harmonics of the spiral spin configuration, which has been missed so far. A realistic spin Hamiltonian, which gives phase diagrams in agreement with experiments, resolves a long standing puzzle, i.e., the double-peak structure of the OS with a larger low-energy peak originating from magnon modes hybridized with the zone-edge state. We a…
The origin of the spiral spin-order in perovskite multiferroic manganites $R$MnO$_{3}$ ($RE=$ Tb or Dy) is here investigated using a two $e_{\rm g}$-orbitals double-exchange model. Our main result is that the experimentally observed spiral phase can be stabilized by introducing a relatively weak next-nearest-neighbor superexchange coupling ($\sim10%$ of the nearest-neighbor superexchange). Moreover, the Jahn-Teller lattice distortion is also shown to be essential to obtain a realistic spiral period. Supporting our conclusions, the generic phase diagram of undoped perovskite manganites is obtai…
Magnetic and dielectric properties on a polycrystalline La0.7Bi0.3CrO3 have been investigated. A canted antiferromagnetic (CAF) phase transition giving weak ferromagnetism at TN = 230K has been observed. M-H at 10K shows non-saturating trend, even up to 5T, confirms the CAF ordering. The permittivity (ε')-vs-temperature (T) variation shows a relaxor ferroelectric (RFE) nature accompanied by a pronounced anomaly in ε'-T at TN. The anomaly in ε'-T at TN indicates the presence of magentoelectric (ME) coupling in this material.
ABO3 perovskite multiferroic La0.5Bi0.5Mn0.5Fe0.5O3.09 where the B-site cations is responsible for the magnetic properties and the A-site cation with lone pair electron is responsible for the ferroelectric properties was synthesized at normal conditions. This oxide exhibits a ferromagnetic transition around 240 K with a well defined hysteresis loop, and a significant reversible remnant polarization below 67K similar to ferroelectric behavior. The magnetic interaction is interpreted by the ferromagnetic Fe3+-O-Mn3+ and antiferromagnetic Fe3+(Mn3+)-O-Fe3+(Mn3+) interactions competed each other, …
First-principles electronic structure calculations have been performed for the double perovskite Bi$_2$CoMnO$_6$ in its non-centrosymmetric polar state using generalized gradient approximation plus Hubbard U approach. We find that while Co is in a high spin state, Mn is in an intermediate spin state. The calculated dynamical charge tensors are anisotropic reflecting a low-symmetry structure of the compound. Magnetic structure dependent phonon frequencies indicate the presence of spin-phonon coupling. Using Berry phase method, we obtain a spontaneous electronic polarization of 5.88 $μC/cm^2$ wh…
The synthesis and structural studies on the polycrystalline La1-xBixCrO3 (x =0, 0.2, 0.25, 0.3, 0.35) have been done using XRD and TEM. The results of the Reitveld refinement of XRD data shows that these compounds crystallize in an orthorhombic structure with Pnma space group. With increasing Bi content, the unit cell volume and lattice parameters undergo non monotonous changes within the tolerance factor from 0.84092 to 0.84072. This has been attributed to the anisotropy induced by lone pair of Bi3+, which may distorted the lattice.
Magnetoelectric phase diagrams of the perovskite manganites, Eu1-xYxMnO3 and Gd1-xTbxMnO3, are theoretically studied. We first construct a microscopic model, and then analyze the model using the Monte-Carlo method. We reproduce the diagrams, which contain two different multiferroic states, i.e., the ab-plane spin cycloid with electric polarization P//a and the bc-plane spin cycloid with P//c. We reveal that their competition originates from a conflict between the single-ion anisotropy and the Dzyaloshinsky-Moriya interaction, which is controlled by the second-neighbor spin exchanges enhanced b…
We report the structural and magnetoelectrical properties of La$_{0.7}$Ca$_{0.3}$MnO$_3$/BaTiO$_3$ perovskite superlattices grown on (001)-oriented SrTiO$_3$ by the pulsed laser deposition technique. Magnetic hysteresis loops together with temperature dependent magnetic properties exhibit well-defined coercivity and magnetic transition temperature (T$_C$) \symbol{126}140 K. $DC$ electrical studies of films show that the magnetoresistance (MR) is dependent on the BaTiO$_3$ thickness and negative $MR$ as high as 30% at 100K are observed. The $AC$ electrical studies reveal that the impedance and …
We demonstrate that ethylammonium copper chloride, (C2H5NH3)2CuCl4, a member of the hybrid perovskite family is an electrically polar and magnetic compound with dielectric anomaly around the Curie point (247 K). We have found large spontaneous electric polarization below this point accompanied with a color change in the sample. The system is also ferroelectric, with large remnant polarization (37μC/cm2) that is comparable to classical ferroelectric compounds. The results are ascribed to hydrogen-bond ordering of the organic chains. The coexistence of ferroelectricity and dominant ferromagnetic…
YBaCuFeO5 is one of the interesting multiferroic compounds, which exhibits magnetic ordering and dielectric anomaly above 200 K. Partial substitution of Fe with other magnetic and non-magnetic ion affects the magnetic and the structural properties of the system. We report detailed investigation of structural, magnetic and dielectric properties of YBaCuFe0.85M0.15O5 (M=Co, Ni and Ga). We observed that the partial replacement of Ni and Co in place of Fe, results in magnetic dilution and broadening of the magnetic transition and shifting towards lower temperature. The replacement of Fe with non-m…
Our first-principles results show that geometric frustration can be induced in thin films of multiferroic BiFeO3. We find that competing magnetic interactions occur in the so-called super-tetragonal phase of this material, which can be grown on strongly-compressive substrates. We show that the frustration level can be tuned by appropriately choosing the substrate; in fact, the three-dimensional spin order gets totally annihilated in a narrow range of epitaxial strains. We argue that the effects revealed here are not exclusive to BiFeO3, and predict that they also occur in multiferroic BiCoO3.
We show that a superstructure of antiferromagnetically interacting Fe$^{3+}$ ($S=5/2$) ions in double perovskites AFe$_{1/2}$M$_{1/2}$O$_{3}$ exhibits a ferrimagnetic ordering below $T_{fe} \approx 5.6J_1$ ($J_1/k_B \sim 50$~K), which is close to room temperature. Small clusters of the same structure exhibit a superparamagnetic behavior at $T \lesssim T_{fe}$. The possibility of formation of such clusters explains the room-temperature (superpara)magnetism in 3$d$-metal based oxides.
Cobalt oxides have long been understood to display intriguing phenomena known as spin-state crossovers, where the cobalt ion spin changes vs. temperature, pressure, etc. A very different situation was recently uncovered in praseodymium-containing cobalt oxides, where a first-order coupled spin-state/structural/metal-insulator transition occurs, driven by a remarkable praseodymium valence transition. Such valence transitions, particularly when triggering spin-state and metal-insulator transitions, offer highly appealing functionality, but have thus far been confined to cryogenic temperatures in…
We study the coexistence of strain- and charge-mediated magnetoelectric coupling in a cobalt (0-7 nm) wedge on ferroelectric [Pb(Mg$_{1/3}$/Nb$_{2/3}$)O$_{3}$]$_{0.68}$-[PbTiO$_{3}$]$_{0.32}$ (011) using surface-sensitive x-ray magnetic circular dichroism spectroscopy at the Co L$_{3,2}$ edges. Three distinct electric field driven remanent magnetization states can be set in the Co film at room temperature. Ab-initio density functional theory calculations unravel the relative contributions of both strain and charge to the observed magnetic anisotropy changes illustrating magnetoelectro-elastic …
By means of magnetic, specific heat and pyroelectric measurements, we report on magnetic ferroelectricity in the quadruple perovskite \namno, characterized by a canted antiferromagnetic (AFM) CE structure. Surprisingly, ferroelectricity is concomitant to a dramatic broadening of the magnetic hysteresis loop, well below the AFM ordering temperature. This unconventional behavior shows that the formation of ferroelectric domains is induced by the symmetric exchange interaction in the local scale, e.g. at magnetic domain boundaries or defects. The value of electric polarization, $P = 0.027 μ$C cm$…
We report cooperative magnetic orderings in a 6H-perovskite multiferroic system, Ba3HoRu2O9, via comprehensive neutron powder diffraction measurements. This system undergoes long-range antiferromagnetic ordering at TN1 ~ 50 K with a propagation wave vector of K1 = (0.5 0 0), a transition temperature much higher than the previously reported one at ~10 K (TN2). Both Ru and Ho-moments order simultaneously below TN1, followed by spin-reorientations at lower temperatures, demonstrating strong Ru(4d)-Ho(4f) magnetic correlation. Below TN1 another magnetic phase with a propagation wave vector K2 = (0…