Polyhydrides offer intriguing perspectives as high-temperature superconductors. Here we report the high-pressure synthesis of a series of lanthanum-yttrium ternary hydrides: cubic hexahydride $(La,Y)H_{6}$ with a critical temperature $T_{C}$ = 237 +/- 5 K and decahydrides $(La,Y)H_{10}$ with a maximum $T_{C}$ ~${253 K}$ and an extrapolated upper critical magnetic field $B_{C2(0)}$ up to ${135 T}$ at 183 GPa. This is one of the first examples of ternary high-$T_{C}$ superconducting hydrides. Our experiments show that a part of the atoms in the structures of recently discovered ${Im3m}$-$YH_{6}$…

Superconductivity at 215 K in lanthanum hydride at high pressures

We synthesized lanthanum hydride (LaHx) by laser heating of lanthanum in hydrogen atmosphere at pressure P = 170 GPa. The sample shows a superconducting step at 209 K and 170 GPa and temperature dependence of resistance. By releasing the pressure to 150 GPa, the superconducting transition temperature Tc increases to 215 K - the record Tc. This finding supports a way of achieving Tc higher than the one in H3S (203 K) in hydrides with sodalite-like structures, first proposed for CaH6 (Tc=245 K) and later for yttrium and lanthanum hydrides where higher, room temperature superconductivity is expec…

高压下高临界温度LaH₁₀±δ薄膜的合成与稳定性

Synthesis and stability of high-$T_c$ LaH$_{10\pmδ}$ films at high pressures

本研究以氨硼烷为氢供体，在高压下通过原位激光加热合成LaH₁₀±δ薄膜，证实其高T_c超导性及时间稳定性，确立PVD薄膜前驱体为氢化物合成的可行途径。

Superconductivity in sodalite-like yttrium hydride clathrates

We report ab-initio calculations of the superconducting properties of two high-Tc sodalite-like clathrate yttrium hydrides, YH6 and YH10, within the fully anisotropic ME theory, including Coulomb corrections. For both compounds we find almost isotropic superconducting gaps, resulting from a uniform distribution of the electron-phonon coupling over phonon modes and electronic states of mixed Y and H character. The Coulomb screening is rather weak, resulting in a Morel-Anderson pseudopotential mu*= 0:11, at odds with claims of unusually large Tc in lanthanum hydrides. The corresponding critical …

Effect of the chemical pressure on superconductivity and SDW in undoped and 15%F doped La1-yYyFeAsO compounds

We present a study concerning the partial substitution of yttrium at the lanthanum site of the undoped LaFeAsO and superconducting LaFeAsO0.85F0.15 compounds. We prepared samples with a nominal yttrium content up to 70% producing simultaneous shrinkage of both the a- and c-lattice parameters by 1.8% and 1.7%, respectively. The chemical pressure provided by the partial substitution with this smaller ion size causes a lowering of the spin density wave temperature in the undoped compounds, as well as an increase of the superconducting transition temperatures in the doped ones. The 15% fluorine-do…

Potential high-$T_{c}$ superconductivity in YCeH$_{x}$ and LaCeH$_{x}$ under pressure

Lanthanum, yttrium, and cerium hydrides are the three most well-known superconducting binary hydrides (La-H, Y-H, and Ce-H systems), which have gained great attention in both theoretical and experimental studies. Recent studies have shown that ternary hydrides composed of lanthanum and yttrium can achieve high superconductivity around 253 K. In this study we employ the evolutionary-algorithm-based crystal structure prediction (CSP) method and first-principles calculations to investigate the stability and superconductivity of ternary hydrides composed of (Y, Ce) and (La, Ce) under high pressure…