Controlling material properties by modulating the crystalline structure has been attempted using various techniques, e.g., hydrostatic pressure, chemical pressure, and epitaxy. These techniques succeed to improve properties and achieve desired functionalities by changing the unit cell in all dimensions. In order to obtain a more detailed understanding on the relation between the crystal lattice and material properties, it is desirable to investigate the influence of a smaller number of parameters. Here, we utilize the combination of chemical pressure and epitaxy to modify a single lattice parameter of the multiferroic orthorhombic RMnO$_3$ (R = rare-earth, o-RMnO$_3$) system. By growing a series of o-RMnO$_3$ (R = Gd - Lu) films coherently on (010)-oriented YAlO$_3$ substrates, the influence of chemical pressure is reflected only along the $b$-axis. Thus, a series of o-RMnO$_3$ with $a$ ~ 5.18 Å, 5.77 Å < $b$ < 5.98 Å, and $c$ ~ 7.37 Å were obtained. Raman spectra analysis reveals that the change of the $b$-axis parameter induces a shift of the oxygen in the nominally "fixed" $ca$-plane. Their ferroelectric ground state is independent on the $b$-axis parameter showing polarization of ~ 1 $μ$C cm$^{-2}$ along the $a$-axis for the above-mentioned range, except for $b$ ~ 5.94 Å which corresponds to TbMnO$_3$ showing ~ 2 $μ$C cm$^{-2}$. This result implies that multiferroic order of o-RMnO$_3$ is almost robust against the $b$-axis parameter provided that the dimension of the $ca$-plane is fixed to 7.37 Å $\times$ 5.18 Å.
Multiferroic materials have received an astonishing attention in the last decades due to expectations that potential coupling between distinct ferroic orders could inspire new applications and new device concepts. As a result, a new knowledge on coupling mechanisms and materials science has dramatically emerged. Multiferroic RMnO3 perovskites are central to this progress providing a suitable platform to tailor spin-spin and spin-lattice interactions. With views towards applications, development of thin films of multiferroic materials have also progressed enormously and nowadays thin film manga…
The present work aims to describe, within a single phenomenological approach, the specific sequence of phase transitions observed in the rare-earth manganites RMnO3 at zero magnetic field. It is shown that a single integrated description of the temperature versus composition phase diagrams of these compounds and related solid solutions can be obtained within the scope of Landau theory by adopting the so called type-II description of the modulated phases.
Hexagonal RMnO3 manganites are improper ferroelectrics in which the electric polarization is a by-product of the tripling of the unit cell. In YMnO3, there is a second transition at ~ 920K whose nature remains unexplained. We argue that this transition can be seen as a sort of hidden order in which a residual symmetry displayed by the trimerization order parameter is spontaneously broken. This additional order gives rise to twelve structural domains instead of six, and structural domain boundaries that can be either ferroelectric or non-ferroelectric domain walls.
Electronic structures of multiferroic RMnO$_3$ (R=Y, Er) have been investigated by employing photoemission spectroscopy (PES) and x-ray absorption spectroscopy (XAS). We have found that Mn ions in RMnO$_3$ are in the trivalent high-spin state with the total spin of S=2. The occupied Mn ($d_{xz} - d_{yz}$) states lie deep below $\rm E_F$, while the occupied Mn ($d_{xy} - d_{x^2 -y^2}$) states overlap very much with the O $2p$ states. It is observed that the PES spectral intensity of Mn 3d states is negligible above the occupied O $2p$ bands, suggesting that YMnO$_3$ is likely to be a charge-tra…
We propose a model for the pair of electromagnon excitations observed in the class of multiferroic materials {\it R}MnO$_3$ ({\it R} is a rare-earth ion). The model is based on a harmonic cycloid ground state interacting with a zone-edge magnon and its twin excitation separated in momentum space by two times the cycloid wave vector. The pair of electromagnons is activated by cross coupling between magnetostriction and spin-orbit interactions. Remarkably, the spectral weight of the twin electromagnon is directly related to the presence of a magnetically induced oscillatory polarization in the g…
Multiferroic hexagonal RMnO3 (R=rare earths) crystals exhibit dense networks of vortex lines at which six domain walls merge. While the domain walls can be readily moved with an applied electric field, the vortex cores were so far impossible to control. Our experiments demonstrate that shear strain induces a Magnus-type force pulling vortices and antivortices in opposite directions and unfolding them into a topological stripe domain state. We discuss the analogy between this effect and the current-driven dynamics of vortices in superconductors and superfluids.
Hexagonal RMnO3 is a multiferroic compound with a giant spin-lattice coupling at an antiferromagnetic transition temperature [1]. Despite extensive studies over the past two decades, however, the origin and underlying microscopic mechanism of the strong spin-lattice coupling remain still very much elusive. In this study, we have tried to address this problem by measuring the thermal expansion and dielectric constant of doped single crystals Y1-xLuxMnO3 with x = 0, 0.25, 0.5, 0.75, and 1.0. From these measurements, we confirm that there is a progressive change in the physical properties with do…
Pressure-induced phase transitions of multiferroic BiFeO3 have been investigated using synchrotron radiation X-ray diffraction with diamond anvil cell technique at room temperature. Present experimental data clearly show that rhombohedral (R3c) phase of BiFeO3 first transforms to monoclinic (C2/m) phase at 7 GPa, then to orthorhombic (Pnma) phase at 11 GPa, which is consistent with recent theoretical ab initio calculation. However, we observe another peak at 2θ=7° in the pressure range of 5-7 GPa that has not been reported previously. Further analysis reveals that this reflection peak is attri…
We use resonant and non-resonant X-ray diffraction measurements in combination with first-principles electronic structure calculations and Monte Carlo simulations to study the relationship between crystal structure and multiferroic orders in the orthorhombic perovskite manganites, o-$R$MnO$_3$ ($R$ is a rare-earth cation or Y). In particular, we focus on how the internal lattice parameters (Mn-O bond lengths and Mn-O-Mn bond angles) evolve under chemical pressure and epitaxial strain, and the effect of these structural variations on the microscopic exchange interactions and long-range magnetic…
Spectrum of coupled spin, acoustic, electro-dipole and electromagnetic waves in orthorhombic perovskite multiferroics placed in external electric and magnetic field has been calculated. Frequency and field dependencies of electric, magnetic, and magnetoelectric susceptibilities of multiferroics with cycloidal antiferromagnetic structure in external electric and magnetic fields have been investigated as well. The spectrum of coupled waves has a band structure. Width and frequency ranges of bands depend on external fields. The possibility of control of electrodynamic properties of orthorhombic p…
Multiferroic properties of orthorhombic HoMnO3 (Pbnm space group) are significantly modified by epitaxial compressive strain along the a-axis. We are able to focus on the effect of strain solely along the a-axis by using an YAlO3 (010) substrate, which has only a small lattice mismatch with HoMnO3 along the other in-plane direction (the c-axis). Multiferroic properties of strained and relaxed HoMnO3 thin films are compared with those reported for bulk, and are found to differ widely. A relaxed film exhibits bulk-like properties such as a ferroelectric transition temperature of 25 K and an inco…
We show that epitaxial (001) thin films of multiferroic bismuth ferrite BiFeO3 are monoclinic at room temperature instead of tetragonal or Rhombohedral as reported earlier . We report a orthorhombic order-disorder beta-phase between 820C and 950C contrary to the earlier report. The transition sequence monoclinic-orthorhombic phase in (001)BiFeO3 thin film (rhombohedral-orthorhombic transition in single crystal) resembles that of BaTiO3 or PbSc1/2Ta1/2O3. The transition to the cubic $γ$-phase causes an abrupt collapse of the bandgap toward zero (insulator-metal transition) at the orthorhombic-c…
High pressure x-ray diffraction (XRD) measurements on RMnO3 (R=Dy, Ho and Lu) reveals that varying structural changes occurs for different R ions. Large lattice changes (orthorhombic strain) occur in DyMnO3 and HoMnO3 while the Jahn-Teller (JT) distortion remains stable. On the other hand, in LuMnO3, Mn-O bond distortions are observed in the region 4-8 GPa with the broad minimum in the JT distortion. High pressure IR measurements indicate that a phonon near 390 cm-1 corresponding to the complex motion of the Mn and O ions changes anomalously for LuMnO3. It softens in the 4-8 GPa region, which …
Structural changes in REMnO3 (RE= Y, Ho, Lu) under high pressure were examined by synchrotron x-ray diffraction methods at room temperature. Compression occurs more readily in the ab plane than along the c-axis. Under hydrostatic pressure (~11 GPa), the atoms hold their approximate ambient fractional positions in the unit cell and the spontaneous polarization shows no significant change. With increased pressure, a pressure-induced hexagonal to orthorhombic phase transition was observed starting at ~ 22GPa for Lu(Y)MnO3. A small volume fraction of Lu(Y)MnO3 is converted to the orthorhombic phas…
We report on structural, magnetic, dielectric, and thermodynamic properties of (Eu:Y)MnO3 for Y doping levels 0 <= x < 1. This system resembles the multiferroic perovskite manganites RMnO3 (with R= Gd, Dy, Tb) but without the interference of magnetic contributions of the 4f-ions. In addition, it offers the possibility to continuously tune the influence of the A-site ionic radii. For small concentrations x <= 0.1 we find a canted antiferromagnetic and paraelectric groundstate. For higher concentrations x <= 0.3 ferroelectric polarization coexists with the features of a long wavelength incommens…
We report X-ray structural studies of the metal-insulator phase transition in bismuth ferrite, BiFeO3, both as a function of temperature and of pressure (931 oC at atmospheric pressure and ca. 45 GPa at ambient temperature). Based on the experimental results, we argue that the metallic gamma-phase is not rhombohedral but is instead the same cubic Pm3m structure whether obtained via high temperature or high pressure, that the MI transition is second order or very nearly so, that this is a band-type transition due to semi-metal band overlap in the cubic phase and not a Mott transition, and that …
We report experimental evidence for pressure instabilities in the model multiferroic BiFeO3 and namely reveal two structural phase transitions around 3 GPa and 10 GPa by using diffraction and far-infrared spectroscopy at a synchrotron source. The intermediate phase from 3 to 9 GPa crystallizes in a monoclinic space group, with octahedra tilts and small cation displacements. When the pressure is further increased the cation displacements (and thus the polar character) of BiFeO3 is suppressed above 10 GPa. The above 10 GPa observed non-polar orthorhombic Pnma structure is in agreement with recen…
We investigated the magnetic structure of an orthorhombic YMnO3 thin film by resonant soft x-ray and hard x-ray diffraction. We observed a temperature-dependent incommensurate magnetic reflection below 45 K and a commensurate lattice-distortion reflection below 35 K. These results demonstrate that the ground state is composed of coexisting E-type and cycloidal states. Their different ordering temperatures clarify the origin of the large polarization to be caused by the E-type antiferromagnetic states in the orthorhombic YMnO3 thin film.
LiCu_2O_2 single crystals were studied in the temperature range 300-1100 K by means of heating-cooling curves of differential thermal analysis (DTA), thermogravimetry (TG), X-ray powder diffraction and electrical measurements. A reversible first-order phase transition between orthorhombic and tetragonal phases was found to take place at 993 K. At the transition, a peak is observed in the DTA curves, as well as jumps of the unit cell parameters and electrical resistivity. Considering the crystal structure of LiCu_2O_2 and the entropy change associated with the phase transition, it is concluded …
We present a detailed study of the structural, electronic, magnetic and ferroelectric properties of prototypical \textit{proper} and \textit{improper} multiferroic (MF) systems such as BiFeO$_{3}$ and orthorhombic HoMnO$_{3}$, respectively, within density functional theory (DFT) and using the Heyd-Scuseria-Ernzerhof hybrid functional (HSE). By comparing our results with available experimental data as well as with state-of-the-art GW calculations, we show that the HSE formalism is able to account well for the relevant properties of these compounds and it emerges as an accurate tool for predicti…
We fabricated epitaxial thin films of hexagonal DyMnO3, which otherwise form in a bulk perovskite structure, via deposition on Pt(111)//Al2O3 (0001) and YSZ(111) substrates: each of which has in-plane hexagonal symmetry. The polarization hysteresis loop demonstrated the existence of ferroelectricity in our hexagonal DyMnO3 films at least below 70 K. The observed 2.2 uC/cm^2 remnant polarization at 25 K corresponded to a polarization enhancement by a factor of 10 compared to that of the bulk orthorhombic DyMnO3. Interestingly, this system showed an antiferroelectric-like feature in its hysteres…
The synthesis and structural studies on the polycrystalline La1-xBixCrO3 (x =0, 0.2, 0.25, 0.3, 0.35) have been done using XRD and TEM. The results of the Reitveld refinement of XRD data shows that these compounds crystallize in an orthorhombic structure with Pnma space group. With increasing Bi content, the unit cell volume and lattice parameters undergo non monotonous changes within the tolerance factor from 0.84092 to 0.84072. This has been attributed to the anisotropy induced by lone pair of Bi3+, which may distorted the lattice.
A series of manganites Tb1-xHoxMnO3 (0<=x<=0.6) with orthorhombic structure are synthesized and detailed investigations on their multiferroicity are performed. Successive magnetic transitions upon temperature variation are evidenced for all samples, and both the Mn3+ spiral spin ordering and rare-earth spin ordering are suppressed with increasing x. Significant enhancement of both the polarization and magnetoelectric response within 0.2<x<0.4 is observed, which may be ascribed to the competition possibly existing between spiral and E-type spin orders. Theoretical calculation is given based on …
The perovskite (1-x)YMnO$_3$-xBiFeO$_3$ binary system is very promising because of its multiferroic end members. Nanocrystalline phases have been recently obtained by mechanosynthesis across the system, and the perovskite structural evolution has been described. Two continuous solid solutions with orthorhombic Pnma and rhombohedral R3c symmetries were found, which coexist within a broad compositional interval of 0.5 < x < 0.9. This might be a polar-nonpolar morphotropic phase boundary region, at which strong phase-change magnetoelectric responses can be expected. A major issue is phase decompo…
Multiferroic bismuth ferrite Bi_2Fe_4O_9 (BFO) ceramic was synthesized by conventional solid state reaction route. X-ray diffraction and Rietveld refinement show formation of single phase ceramic with orthorhombic crystal structure (space group Pbam). The morphological study depicted a well-defined grain of size $\simeq$2μm. The optical studies were carried out by using UV-Vis spectrophotometer which shows a band gap of 1.53 eV and a green emission spectrum at 537 is observed in the Photoluminescence study. The frequency dependent dielectric study at various temperature revealed that the diele…
The magnetic, dielectric and structural properties of type-I multiferroic KNiPO$_4$ have been investigated by neutron powder diffraction, magnetization, dielectric and high temperature synchrotron-XRD measurements. Below the Néel transition of $T_\mathrm{N}$ = 25 K, KNiPO$_4$ displays a weakly non-collinear antiferromagnetic (AFM) structure with the orientation of the Ni$^{2+}$ magnetic moments mainly along $a$ axis. The compound crystallizes in the polar orthorhombic $Pna2_1$ space group at room temperature. A second-order structural phase transition corresponding to the onset ferroelectricit…
The orthorhombic Haldane spin chain compound Tb2BaNiO5 (Neel order, TN1= 63 K) has been shown to be an exotic multiferroic system below (TN2) 25 K due to various fascinating features, pointing to a strong potential for the advancement of concepts in this field. In particular, the rare-earth ions play a direct decisive role unlike in many other well known multiferroic materials and there appears to be a critical canting angle, developing below TN2, subtended by Tb 4f and Ni 3d moments to trigger this cross coupling phenomenon. However, for a small replacement of Sr for Ba, viz. in Tb2Ba0.9Sr0.1…
The interaction of coexisting structural instabilities in multiferroic materials gives rise to intriguing coupling phenomena and extraordinarily rich phase diagrams, both in bulk materials and strained thin films. Here we investigate the multiferroic BiMnO3 with its peculiar 6s2 electrons and four interacting mechanisms: electric polarity, octahedra tilts, magnetism, and cooperative Jahn-Teller distortion. We have probed structural transitions under high pressure by synchrotron x-ray diffraction and Raman spectroscopy up to 60 GPa. We show that BiMnO3 displays under pressure a rich sequence of…
Effect of an internal chemical pressure on structural, optical, magnetic and electrical properties in Bi0.9RE0.1FeO3 Ceramics (RE =Gd3+,Tb3+,Dy3+)has been studied extensively. Some of the highlights are as follows; 1. Coexistence of orthorhombic Bragg reflections along with the R3c phase.(Structural Phase separation revealed from XRD and Raman spectroscopy) 2. Selective softening of phonon mode corresponding to oxygen motion suggests a significant destabilization in the FeO6 octahedra. 3. Three Charge transfer transitions (Fe1 3d\rightarrow Fe2 3d, Op \rightarrow Fed,Op \rightarrow Bip) and a …
Ferroelectric materials possess a spontaneous electric polarization and may be utilized in various technological applications ranging from non-volatile memories to solar cells and light polarizers. Recently, hexagonal rare-earth manganites, h-RMnO$_3$ (R is a rare-earth ion) have attracted considerable interest due to their intricate multiferroic properties and improper ferroelectricity characterized by a sizable remnant polarization and high Curie temperature. Here, we demonstrate that these compounds can serve as very efficient photovoltaic materials and, in addition, possess remarkable opti…
The crystal structure and magnetic properties of the RbMnPO4 zeolite-ABW type material have been studied by temperature-dependent neutron powder diffraction, low temperature magnetometry and heat capacity measurements. RbMnPO4 represents a rare example of a weak ferromagnetic polar material, containing Mn2+ ions with TN = 4.7 K. The neutron powder diffraction pattern recorded at T = 10 K shows that the compound crystallizes in the chiral and polar monoclinic space group P21 (No. 4) with the unit-cell parameters: a = 8.94635(9) Å, b = 5.43415(5) Å, c = 9.10250(8) Å and beta = 90.4209(6)°. A clo…
A low-temperature setup for lock-in technique based dynamic magnetoelectric coupling measurements
Indian Institute of Technology, Delhi（印度德里理工学院）；Government Girls Polytechnic, Bulandshahr（布兰德尔沙尔国立女子理工学院）；Institute for Materials Research, Tohoku University（东北大学材料研究所）
Solid solutions of (1-x)LaFeO3-(x)PbTiO3 (0<x<1) have been prepared by conventional solid-state reaction. These complex perovskites have been studied by means of X-ray (XRPD) and neutron powder (NPD) diffraction, complemented with dielectric, magnetic, heat capacity and Mössbauer measurements. Complete solubility in the perovskite series was demonstrated. The NPD and XRPD patterns were successfully refined as orthorhombic (x \leq 0.7) and tetragonal (x \geq 0.8). A composition-driven phase transformation occurs within the interval 0.7<x<0.8. The samples with x<0.5 showed evidence of long-range…
By means of single-crystal X-ray diffraction we have revealed the breaking of centrosymmetry when lowering the temperature under T$_s$ = 200 K concomitantly with the setting of a commensurate superstructure in the small A-site quadruple perovskite YMn$_3$Mn$_4$O$_{12}$. This results is in agreement with all data already reported for this compounds and solve the previous inconsistency about the Yttrium position. The superstructure is characterized by the appearing of satellite reflections in the single crystal pattern, consistent with an I-centered pseudo-orthorhombic commensurate supercell wit…