在常压和0.35 K ~室温范围内，用热力学和磁学测量方法研究了Ce $_2$ Rh $_{1-x}$ Pd $_x$ In $_8$固溶体在整个浓度范围内的磁性和超导电性的演化.为此目的，已从In自熔剂中生长出Pd浓度x = 0，0.10，0.15，0.30，0.45，0.55，0.85和1的单晶，并用X射线衍射和微探针分析表征。从反铁磁体Ce $_2$ RhIn $_8$开始，Néel温度随着Pd浓度的增加而逐渐降低，并且$x \ge 0.45$的反铁磁性已经消失。只有Ce $_2$ PdIn $_8$具有超导电性。
英文摘要：
The evolution of magnetism and superconductivity in Ce$_2$Rh$_{1-x}$Pd$_x$In$_8$ solid solutions has been studied within the entire concentration range by means of thermodynamic and magnetic measurements at ambient pressure and at temperatures between 0.35 K and room temperature. For this purpose, single crystals with Pd concentrations x = 0, 0.10, 0.15, 0.30, 0.45, 0.55, 0.85 and 1 have been grown from In self-flux and characterized by x-ray diffraction and microprobe analysis. Starting from the antiferromagnet Ce$_2$RhIn$_8$, the Néel temperature gradually decreases with increasing Pd concentration and the antiferromagnetism has disappeared for $x \ge 0.45$. Superconductivity has been observed only for Ce$_2$PdIn$_8$.
Possible ferrimagnetism and ferroelectricity of half-substituted rare-earth titanate: a first-principles study on Y$_{0.5}$La$_{0.5}$TiO$_3$
具有钙钛矿结构的钛酸盐，包括铁电体（例如，BaTiO $_3$）和铁磁材料（例如，YTiO（$_3$）是重要的功能材料。最近的理论研究预测了应变EuTiO $_3$和钛酸盐超晶格中的多铁性态，其中前者已经被实验证实。在这里，第一性原理计算进行调查Y半取代的LaTiO 3的结构，磁性和电子性质。我们的研究结果表明，由于固有的相竞争，Y $_{0.5}$ La $_{0.5}$ TiO $_3$的磁性敏感地依赖于其结构细节。最低能态是铁磁态，导致0.25 $μ_{\rm B}$ /Ti。此外，Y $_{0.5}$ La $_{0.5}$ TiO $_3$的某些构型表现出混合的非正常极化，这可以显著地受到磁性的影响，从而导致多铁性。由于取代的猝灭无序，具有随机A位离子的真正Y $_{0.5}$ La $_{0.5}$ TiO 3材料可能表现出有趣的弛豫行为。
Emergent magnetism, heavy electrons and pressure-induced reentrant superconductivity in the iron substituted 4d transition-metal sulfides
Zhejiang University of Technology（浙江工业大学）；Fudan University（复旦大学）；Qufu Normal University（曲阜师范大学）；Nanjing University of Posts and Telecommunications（南京邮电大学）；Suzhou University of Technology（苏州科技大学）；Hangzhou Dianzi University（杭州电子科技大学）；National Taiwan Normal University（台湾师范大学）；Academia Sinica（中央研究院）；Zhejiang University（浙江大学）；Ningbo University（宁波大学）；Hangzhou Normal University（杭州师范大学）；Shanghai Jiao Tong University（上海交通大学）
Structure and magnetism of the skyrmion hosting family GaV$_4$S$_{8-y}$Se$_y$ with low levels of substitutions between $0 \leq y \leq 0.5$ and $7.5 \leq y\leq 8$
为了研究它们的磁性和结构性质，合成了在$0 \leq y \leq 0.5$和$7.5 \leq y\leq 8$之间具有小水平取代的GaV $_4$ S $_{8-y}$ Se $_y$材料家族的多晶成员。取代的skyrmion托管母体化合物GaV $_4$ S $_8$和GaV $_4$ Se $_8$，发现抑制温度的立方菱形结构的相变发生在两个末端化合物，并创建一个温度区域周围的过渡，其中有一个共存的这两个阶段。类似地，磁化强度的大小和磁性转变的温度在所有取代的化合物中都被抑制，直到实现玻璃状磁性状态。有证据表明，从$ac$的磁化率数据，skyrmion晶格与那些在GaV $_4$ S $_8$和GaV $_4$ Se $_8$类似的动力学是目前在化合物具有非常低的水平的取代，$0 < y< 0.2$和$7.8 < y < 8$，然而，这些国家消失在更高水平的取代。这些取代的材料的磁性受到取代的影响，改变交换途径，并导致越来越无序的磁性状态的产生。
Magnetism and electronic dynamics in $CuCr_{2-x}Sn_xS_4$ spinels studied by transferred hyperfine fields at $^{119}Sn$ and muon spin rotation and relaxation
Phase equilibria in MnSb2Te4-GeSb2Te4 system and magnetic properties of Mn1-xGexSb2Te4 solid solutions
French-Azerbaijani University (UFAZ)（法阿联合大学）；Azerbaijan State Oil and Industry University (ASOIU)（阿塞拜疆国立石油工业大学）；Institute of Catalysis and Inorganic Chemistry (ICIC), Azerbaijan National Academy of Sciences (ANAS)（阿塞拜疆科学院催化与无机化学研究所）；Azerbaijan State University of Economics (UNEC)（阿塞拜疆国立经济大学）
Anomalous dependence of the c-axis polarized Fe B$_{1g}$ phonon mode with Fe and Se concentrations in Fe$_{1+y}$Te$_{1-x}$Se$_x$
我们报告了一系列Fe $_{1+y}$ Te $_{1-x}$ Se $_{x}$化合物的晶格动力学性质的研究，特别强调了具有B $_{1g}$对称性的Fe的c轴极化振动，这是所有Fe基超导体家族共有的拉曼活性模式。我们已经进行了系统的研究，作为Se $x$和过量的Fe $y$浓度的函数，这种声子模式的温度依赖性。在母体化合物Fe $_{1+y}$ Te中，我们观察到了一个非常规的声子加宽之间的室温和磁有序温度$T_N$。当Te取代Se，长程磁序被超导性取代时，这种情况平稳地向规则的非谐行为发展。无论硒含量，过量的铁示出提供一个额外的阻尼通道的B $_{1g}$声子在低温下。在局域密度近似（LDA）下，采用密度泛函理论（DFT）从头计算方法，在虚晶近似（VCA）下计算了含铁离子的声子频率，包括磁性极化率和非化学计量比。我们得到了一个很好的协议与测量的声子频率在Fe不足的样品，而Fe过量的影响是很差的再现。这可能是由于过量的铁引起的局部磁性和低能量的磁波动，不能准确地处理这些方法。正如最近的中子散射和$μ$ -SR研究所揭示的，这些现象发生在观察到B $_{1g}$声子异常衰变的温度范围内，并表明这种模式与Fe $_{1+y}$ Te $_{1-x}$ Se $_{x}$中的局部磁矩和自旋涨落的特殊耦合。