We have performed magneto-optical Kerr spectroscopy measurements on intercalated transition-metal dichalcogenide Fe$_{0.25}$TaS$_{2}$ in the polar Kerr geometry as a function of temperature, magnetic field, and wavelength. The Kerr angle exhibits pronounced peaks at $\sim$775 nm (1.6 eV) and $\sim$515 nm (2.4 eV), which we attribute to spin-dependent interband optical transitions arising from states in the vicinity of the Fermi energy. Below the ferromagnetic transition temperature (165 K), we observe strongly wavelength- and magnetic-field-dependent Kerr signal. At a fixed wavelength, the magnetic-field dependence of the Kerr angle shows a clear hysteresis loop, but its shape sensitively changes with the wavelength. We propose a model that takes into account contributions from domain walls, which allowed us to derive a mathematical expression that successfully fits all the observed hysteresis loops.
Magnetoelectric Effect driven by Magnetic Domain Modification in LuFe2O4
利用交流阻抗谱研究了LuFe 2 O 4单晶的磁电容效应。在磁场作用下，本征阻抗响应可与界面响应分离，并在TFerri ~ 240 K以下显示出明显的磁滞回线。磁场作用下的中子衍射实验证实了介电性质的起源与纳米尺度的铁磁畴边界运动有关。这些结果表明，微观畴结构的修改是负责在LuFe 2 O 4的磁电效应。
A structural hysteresis in the charge density wave transition of 1T-TaS2
在准二维1 T-TaS 2（电荷密度波（CDW）原型）中，从无公度（ICDW）到近公度（NCCDW）以及从NCDW到公度（CCDW）的转变分两步进行，并锁定在电阻率的阶跃行为中。在NCDW到CCDW转变的电阻率中观察到的滞后根源于结构滞后，其中通过中子和X射线衍射揭示了sqrt（13）a x sqrt（13）a超结构的局部扭曲。结构滞后是由于错误的大卫星（SODs），因为Ta位移远离完美的三角几何形状以及平面S扭曲。此外，超结构表现出3co层堆叠顺序，减弱变暖和完全消失在ICDW状态。
Probing magnetic anisotropy and spin-reorientation transition in 3D antiferromagnet, Ho$_{0.5}$Dy$_{0.5}$FeO$_{3}\vert$Pt using spin Hall magnetoresistance
Non-equilibrium hysteresis and spin relaxation in the mixed-anisotropy dipolar coupled spin-glass LiHo$_{0.5}$Er$_{0.5}$F$_{4}$
我们提出了一个研究模型自旋玻璃LiHo $_{0.5}$ Er $_{0.5}$ F $_4$同时使用交流磁化率，磁化强度和磁热效应测量以及小角中子散射（SANS）在亚开尔文温度。所有测得的批量揭示滞后行为时，沿晶体学c轴施加的字段。此外，雪崩般的松弛后，从零场冷却状态斜坡到$200 - 300$ Oe的静态字段中观察到。SANS测量被用来跟踪整个磁滞回线和相关的松弛微观自旋重构。将SANS数据与在一百万个晶胞的盒子上进行的非均匀平均场计算进行比较，提供了自旋组态的真实空间图像。我们发现雪崩是由释放的塞曼能量驱动的，塞曼能量加热样品并产生正反馈，继续雪崩。SANS和平均场模拟的组合表明，传统的集群大小的分布被一个中间集群大小耗尽的磁滞回线。
Field induced first order antiferromagnetic to ferromagnetic transition in Al-doped CeFe$_2$: a calorimetric investigation
研究了Ce（Fe $_{0.094}$ Al $_{0.04}$）$_2$多晶样品在固定温度下的场致热容变化，以确定场致一级相变的起源。在4.5K和3.5K下的热容在不同的场循环中表现出滞后，原始曲线停留在包络曲线之外。这类似于在该系统中观察到的磁化和磁阻行为，其中磁滞的量和零场不可逆性的大小分别归因于过冷/过热的程度，以及在场减少循环中从铁磁到反铁磁状态的反向转变的动力学停滞的程度。然而，相反的磁化和磁阻，在热容量这两个功能都随着温度的降低而降低，这意味着结构贡献的重要性。
Anisotropic hysteretic Hall-effect and magnetic control of chiral domains in the chiral spin states of Pr$_2$Ir$_2$O$_7$
我们发现Pr $_2$ Ir $_2$ O $_7$的手征自旋态的反常霍尔效应（AHE）和磁电阻都具有很强的各向异性.在零磁场下低于1.5 K时出现的AHE显示出磁滞现象，这对于沿[111]方向循环的场最为明显。这种滞后是兼容的领域组成的3-在1-出自旋状态，保持共存的2-在2-出自旋冰流形，一旦该领域被删除的场诱导的增长。只有在[111]方向上施加磁场时，我们才观察到一个大的正磁阻和在变磁临界场以上的Shubnikov de Haas振荡。这些观察结果表明，场致自旋织构重构的电子结构的传导电子。