Indications of room-temperature superconductivity at a metal-PZT interface

Dissipative-regime measurements as a tool for confirming and characterizing near-room-temperature superconductivity

The search for new superconducting materials approaching room temperature benefits from having a variety of testing methodologies to confirm and characterize the presence of superconductivity. Often the first signatures of new superconducting species occur incompletely and in very small volume fractions. These trace amounts may be too weak to produce an observable Meissner effect and the resistance may not go completely to zero if the percolation threshold is not met. Under these conditions, secondary behavior--such as transitions or cross overs in the temperature dependence of magnetoresistan…

A15 Nb$_3$Si -- A "high" Tc superconductor synthesized at a pressure of one megabar and metastable at ambient conditions

A15 Nb$_3$Si is, until now, the only high temperature superconductor produced at high pressure (~110 GPa) that has been successfully brought back to room pressure conditions in a metastable condition. Based on the current great interest in trying to create metastable-at-room-pressure high temperature superconductors produced at high pressure, we have restudied explosively compressed A15 Nb$_3$Si and its production from tetragonal Nb$_3$Si. First, diamond anvil cell pressure measurements up to 88 GPa were performed on explosively compressed A15 Nb$_3$Si material to trace Tc as a function of pre…

Low-Frequency Optical Properties of $β^{\prime\prime}$-(BEDO- TTF)$_5$[CsHg(SCN)$_4$]$_2$: Indications of Electronic Correlations in a 1/5-Filled Two-Dimensional Conductor

The polarized reflectivity of $β^{\prime\prime}$-(BEDO-TTF)$_5$[CsHg(SCN)$_4$]$_2$ is studied in the infrared range between 60 cm-1 and 6000 cm-1 from room temperature down to 10 K. Already at T=300 K a pseudogap in the optical conductivity is present of about 300 cm-1; the corresponding maximum in the spectrum shifts to lower frequencies as the temperature decreases. In contrast to quarter-filled BEDT-TTF-based conductors of the $β^{\prime\prime}$-phase a robust Drude component in the conductivity spectra is observed which we ascribe to the larger fraction of charge carriers associated with t…

假定的室温超导体Pb$_9$Cu(PO$_4$)$_6$O的电子结构

Electronic structure of the putative room-temperature superconductor Pb$_9$Cu(PO$_4$)$_6$O

本文通过DFT计算研究了LK-99的电子结构，发现其Cu$^{2+}$的3d$^9$构型形成穿过费米能级的平坦能带，表明未掺杂时该材料为Mott或电荷转移绝缘体，掺杂后可能支持平带超导。