SrFe_2As_2的磁性可以通过Co或Ni少量取代Fe的电子掺杂来抑制，从而产生超导电性。我们证明，大量的替代Fe的等价钌同样抑制磁有序SrFe 2-xRuxAs 2，并导致体超导0.6 <= x <= 0.8。磁化强度、电阻率和比热数据显示Tc高达约20 K。详细的结构研究表明，随着x的增加，晶格参数比c/a强烈下降。DFT能带结构计算与SrFe 2-xRuxAs 2中的磁序仅在大x时不稳定的观察一致。
英文摘要：
The magnetism in SrFe2As2 can be suppressed by electron doping through a small substitution of Fe by Co or Ni, giving way to superconductivity. We demonstrate that a massive substitution of Fe by isovalent ruthenium similarly suppresses the magnetic ordering in SrFe2-xRuxAs2 and leads to bulk superconductivity for 0.6 <= x <= 0.8. Magnetization, electrical resistivity, and specific heat data show Tc up to approx 20K. Detailed structural investigations reveal a strong decrease of the lattice parameter ratio c/a with increasing x. DFT band structure calculations are in line with the observation that the magnetic order in SrFe2-xRuxAs2 is only destabilized for large x.
我们研究了BaFe 2As 2（122）铁砷化物中第5族的化学取代，以努力理解为什么该化合物的Fe位空穴掺杂（例如，使用组5或6）不产生体超导性。我们发现，随着V，Nb或Ta的替代，BaFe 2As 2的c晶格参数增加; c的减少预测了体超导性的缺乏[1]，这通过传输和磁化结果得到了证实。然而，我们的光谱测量发现，在V-122的反铁磁和局部超导纳米级区域的共存，观察到的第一次在过渡金属空穴掺杂的砷化铁。在BaFe 2 As 2中，局部参数（如成分和晶格应变）、平均晶格细节和体量子态（如超导性和磁性）的出现之间存在复杂的联系。[1]L. M. N. Konzen，和A. S. Sefat，J. Phys.：康登斯2017年第29期，第083001页。
The role of different negatively charged layers in Ca10(Fe1-xPtxAs)10(Pt3+yAs8) and superconductivity at 30 K in electron-doped (Ca0.8La0.2)10(FeAs)10(Pt3As8)
Superconductivity by transition metal doping in Ca$_{10}$(Fe$_{1-x}$M$_x$As)$_{10}$(Pt$_3$As$_8$) (M = Co, Ni, Cu)
我们报道了在1038相母体化合物Ca $_{10}$（FeAs）$_{10}$中成功地用钴、镍和铜取代铁（Pt $_3$作为$_8$），产生Ca $_{10}$（Fe $_{1-x}$ Co $_x$ As）$_{10}$（铂$_3$作为$_8$），钙$_{10}$（Fe $_{1-x}$ Ni $_x$ As）$_{10}$（Pt $_3$ As $_8$）和Ca $_{10}$（Fe $_{1-x}$ Cu $_x$ As）$_{10}$（Pt $_3$ As $_8$）。在Co和Ni掺杂的化合物中诱导超导电性，达到高达15 K的临界温度，类似于已知的Pt取代的Ca $_{10}$（Fe $_{1-x}$ Pt $_x$ As）$_{10}$（Pt $_3$ As $_8$），而在Ca $_{10}$（Fe $_{1-x}$ Cu $_x$ As）$_{10}$（Pt $_3$ As $_8$）中没有检测到超导电性。所获得的Tc（x）相图与其他砷化铁超导体的相图非常相似，表明尽管1038型化合物的结构更复杂，但具有相当普遍的行为，其中物理性质主要由FeAs层决定。